Efficient control of ultrafast optical nonlinearity of reduced graphene oxide by infrared reduction

Journal Article · Thu Jul 07 00:00:00 EDT 2016 · Journal of Applied Physics

DOI:https://doi.org/10.1063/1.4955140· OSTI ID:22597883

Bhattachraya, S.; Maiti, R.; Das, A. C.; Saha, S.; Mondal, S.; Ray, S. K.; Bhaktha, S. N. B.

Simultaneous occurrence of saturable absorption nonlinearity and two-photon absorption nonlinearity in the same medium is well sought for the devices like optical limiter and laser mode-locker. Pristine graphene sheet consisting entirely of sp{sup 2}-hybridized carbon atoms has already been identified having large optical nonlinearity. However, graphene oxide (GO), a precursor of graphene having both sp{sup 2} and sp{sup 3}-hybridized carbon atom, is increasingly attracting cross-discipline researchers for its controllable properties by reduction of oxygen containing groups. In this work, GO has been prepared by modified Hummers method, and it has been further reduced by infrared (IR) radiation. Characterization of reduced graphene oxide (RGO) by means of Raman spectroscopy, X-ray photoelectron spectroscopy, and UV-Visible absorption measurements confirms an efficient reduction with infrared radiation. Here, we report precise control of non-linear optical properties of RGO in femtosecond regime with increased degrees of IR reduction measured by open aperture z-scan technique. Depending on the intensity, both saturable absorption and two-photon absorption effects are found to contribute to the non-linearity of all the samples. Saturation dominates at low intensity (∼127 GW/cm{sup 2}) while two-photon absorption becomes prominent at higher intensities (from 217 GW/cm{sup 2} to 302 GW/cm{sup 2}). The values of two-photon absorption co-efficient (∼0.0022–0.0037 cm/GW for GO, and ∼0.0128–0.0143 cm/GW for RGO) and the saturation intensity (∼57 GW/cm{sup 2} for GO, and ∼194 GW/cm{sup 2} for RGO) increase with increasing reduction, indicating GO and RGO as novel tunable photonic devices. We have also explained the reason of tunable nonlinear optical properties by using amorphous carbon model.

• OSTI ID: 22597883
• Journal Information: Journal of Applied Physics, Vol. 120, Issue 1; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
• Country of Publication: United States
• Language: English

Related Subjects

71 CLASSICAL AND QUANTUM MECHANICS
GENERAL PHYSICS
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION
APERTURES
CONTROL
GRAPHENE
INFRARED RADIATION
LASERS
NONLINEAR OPTICS
NONLINEAR PROBLEMS
OPTICAL PROPERTIES
OXIDES
OXYGEN
PHOTONS
RAMAN SPECTROSCOPY
REDUCTION
X-RAY PHOTOELECTRON SPECTROSCOPY