Assessing the potential of group 13 and 14 metal/metalloid phthalocyanines as hole transport layers in organic light emitting diodes
- Department of Chemical Engineering and Applied Chemistry, University of Toronto, 200 College Street, Toronto, Ontario M5S 3E5 (Canada)
In this study, we have assessed the potential application of group 13 and 14 metal and metalloid phthalocyanines ((X){sub n}-MPcs) and their axially substituted derivatives as hole-transporting layers in organic light emitting diodes (OLEDs). OLEDs studied herein have the generic structure of glass/ITO/(N,N′-di(1-naphthyl)-N,N′-diphenyl-(1,1′-biphenyl)-4,4′-diamine (NPB) or (X){sub n}-MPc)(50 nm)/Alq{sub 3} (60 nm)/LiF (1 nm)/Al (80 nm), where X is an axial substituent group. OLEDs using chloro aluminum phthalocyanine (Cl-AlPc) showed good peak luminance values of 2620 ± 113 cd/m{sup 2} at 11 V. To our knowledge, Cl-AlPc has not previously been shown to work as a hole transport material (HTL) in OLEDs. Conversely, the di-chlorides of silicon, germanium, and tin phthalocyanine (Cl{sub 2}-SiPc, Cl{sub 2}-GePc, and Cl{sub 2}-SnPc, respectively) showed poor performance compared to Cl-AlPc, having peak luminances of only 38 ± 4 cd/m{sup 2} (12 V), 23 ± 1 cd/m{sup 2} (8.5 V), and 59 ± 5 cd/m{sup 2} (13.5 V), respectively. However, by performing a simple axial substitution of the chloride groups of Cl{sub 2}-SiPc with pentafluorophenoxy groups, the resulting bis(pentafluorophenoxy) silicon phthalocyanine (F{sub 10}-SiPc) containing OLED had a peak luminance of 5141 ± 941 cd/m{sup 2} (10 V), a two order of magnitude increase over its chlorinated precursor. This material showed OLED characteristics approaching those of a baseline OLED based on the well-studied triarylamine NPB. Attempts to attach the pentafluorophenoxy axial group to both SnPc and GePc were hindered by synthetic difficulties and low thermal stability, respectively. In light of the performance improvements observed by simple axial substitution of SiPc in OLEDs, the use of axially substituted MPcs in organic electronic devices remains of continuing interest to us and potentially the field in general.
- OSTI ID:
- 22594603
- Journal Information:
- Journal of Applied Physics, Vol. 119, Issue 14; Other Information: (c) 2016 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Alternative p-doped hole transport material for low operating voltage and high efficiency organic light-emitting diodes
Highly efficient blue OLEDs based on diphenylaminofluorenylstyrenes end-capped with heterocyclic aromatics
Related Subjects
GENERAL PHYSICS
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ALUMINIUM
BIPHENYL
CHLORIDES
CHLORINE
COMPARATIVE EVALUATIONS
ELECTRONIC EQUIPMENT
GERMANIUM
GLASS
LAYERS
LIGHT EMITTING DIODES
LITHIUM FLUORIDES
PEAKS
PHTHALOCYANINES
PRECURSOR
SILICON
STABILITY
TIN