A novel single-phase white phosphor NaBaBO{sub 3}:Dy{sup 3+},K{sup +} for near-UV white light-emitting diodes
- School of Energy Research, Xiamen University, Xiamen 361005 (China)
Highlights: • A white phosphor NaBaBO{sub 3}:Dy{sup 3+},K{sup +} with CIE coordinate (0.301, 0.308) was synthesized. • The optimum doping concentration of Dy{sup 3+} ions was found. • The effect and mechanism of K{sup +} ion as a charge compensator were discussed. • Temperature-dependent PL property of NaBaBO{sub 3}:Dy{sup 3+},K{sup +} was studied. • PL decay and quantum efficiency behaviors of the samples were investigated. - Abstract: A novel Dy{sup 3+}-doped NaBaBO{sub 3} white-emitting phosphor has been prepared by high temperature solid-state reaction method. The phase structure and luminescence properties of NaBaBO{sub 3}:Dy{sup 3+},K{sup +} samples were investigated. Photoluminescence results show that the as-prepared samples could be effectively excited by near-ultraviolet (NUV) light and generate white light emission due to the {sup 4}F{sub 9/2} → {sup 6}H{sub 15/2} (blue) transition and {sup 4}F{sub 9/2} → {sup 6}H{sub 13/2} (yellow) transition of Dy{sup 3+} ions, respectively. The optimum doping concentration of Dy{sup 3+} ions in the NaBaBO{sub 3} host was determined to be 5.0 mol% and the CIE chromaticity of the sample was determined to be (0.301, 0.308). Moreover, the mechanism of K{sup +} ion as a charge compensator on the improvement of photoluminescence property and the effect of temperature on the photoluminescence property of NaBaBO{sub 3}:Dy{sup 3+},K{sup +} were investigated. Furthermore, photoluminescence decay and quantum efficiency behaviors of NaBaBO{sub 3}:Dy{sup 3+},K{sup +} were also studied. The present work demonstrates that the NaBaBO{sub 3}:Dy{sup 3+},K{sup +} phosphor is a potential candidate for NUV white light emitting diodes.
- OSTI ID:
- 22584246
- Journal Information:
- Materials Research Bulletin, Vol. 73; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Near white light emitting ZnAl{sub 2}O{sub 4}:Dy{sup 3+} nanocrystals: Sol–gel synthesis and luminescence studies
Synthesis and photoluminescence properties of Dy{sup 3+} doped white light emitting CdTa{sub 2}O{sub 6} phosphors
Related Subjects
BARIUM COMPOUNDS
BORATES
CONCENTRATION RATIO
DOPED MATERIALS
DYSPROSIUM IONS
INORGANIC COMPOUNDS
LIGHT EMITTING DIODES
OPTICAL PROPERTIES
PHOSPHORS
PHOTOLUMINESCENCE
POTASSIUM IONS
QUANTUM EFFICIENCY
SODIUM COMPOUNDS
TEMPERATURE DEPENDENCE
ULTRAVIOLET RADIATION
VISIBLE RADIATION