Effect of AlP coating on electrochemical properties of LiMn{sub 2}O{sub 4} cathode material for lithium ion battery
Highlights: • Modified LiMn{sub 2}O{sub 4} surface with AlP successfully. • AlP coating surface modification enhances the cycling stability of LiMn{sub 2}O{sub 4} at both room temperature and 60 °C. • AlP coating surface modification improves the rate capability of LiMn{sub 2}O{sub 4}. - Abstract: AlP-modified LiMn{sub 2}O{sub 4} has been synthesized via a simple chemical deposition method followed by high-temperature heating. The X-ray diffraction patterns, SEM images and Energy Dispersive Spectrometer show the successful surface coating of LiMn{sub 2}O{sub 4} by F-43 m crystal form AlP. AlP-modified LiMn{sub 2}O{sub 4} has a high discharge capacity of 125.7 mAh g{sup −1} with retention of 87% at a current density of 1C between 3.3 V and 4.3 V after 100 cycles at 60 °C, while bare LiMn{sub 2}O{sub 4} has more than 28% capacity loss. At 10 rates, the coated sample delivers capacity of 100 mAh g{sup −1}, which is much higher than bare LiMn{sub 2}O{sub 4}. Based on the EIS (electrochemical impedance spectroscopy) result, AlP coating can effectively inhibit the increase of the charge transfer resistance during charging and discharging cycles.
- OSTI ID:
- 22581444
- Journal Information:
- Materials Research Bulletin, Vol. 74; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preparation of micron-sized Li{sub 4}Ti{sub 5}O{sub 12} and its electrochemistry in polyacrylonitrile electrolyte-based lithium cells
M{sup 3+}-modified LiMn{sub 2}O{sub 4} spinel intercalation cathodes. 2: Electrochemical stabilization by Cr{sup 3+}