Diffusion of 3D-transition elements in Ti-54at%Al
- Changwon National Univ. (Korea, Republic of). Dept. of Materials Science and Engineering
- Tohoku Univ., Sendai (Japan). Dept. of Materials Science
- Korea Inst. of Machinery and Metals, Changwon (Korea, Republic of). Dept. of Materials Engineering
The diffusion coefficients of iron, cobalt, manganese and chromium in Ti-54at%Al alloy were measured over the temperature range from 1,000 to 1,540 K. This study used the radioactive tracers {sup 59}Fe, {sup 57}Co, {sup 54}Mn and {sup 51}Cr and employed the serial the radio-frequency sputter-microsectioning method to measure the penetration profiles of the radioisotope into the specimen. The temperature dependence of the diffusion coefficients was analyzed to be expressed by the following Arrhenius equations: D{sub Fe/TiAl} = (1.3 {times} 10{sup {minus}3}) exp ({minus}363 kJ mol{sup {minus}1}/RT) m{sup 2}/s, D{sub Co/TiAl} = (1.1 {times} 10{sup {minus}3}) exp ({minus}318 kJ mol{sup {minus}1}/RT) m{sup 2}/s, D{sub Mn/TiAl} = (1.2 {times} 10{sup {minus}3}) exp ({minus}326 kJ mol{sup {minus}1}/RT) m{sup 2}/s, D{sub Cr/TiAl} = (4.4 {times} 10{sup {minus}3}) exp ({minus}350 kJ mol{sup {minus}1}/RT) m{sup 2}/s.
- OSTI ID:
- 225093
- Report Number(s):
- CONF-950201--; ISBN 0-87339-304-X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Diffusion of vanadium, chromium, and manganese in copper
Temperature-dependent rate constants for the reactions of gas-phase lanthanides with O{sub 2}