Study of SiO{sub 2}/4H-SiC interface nitridation by post-oxidation annealing in pure nitrogen gas
- Graduate School of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871 (Japan)
An alternative and effective method to perform interface nitridation for 4H-SiC metal-oxide-semiconductor (MOS) devices was developed. We found that the high-temperature post-oxidation annealing (POA) in N{sub 2} ambient was beneficial to incorporate a sufficient amount of nitrogen atoms directly into thermal SiO{sub 2}/SiC interfaces. Although N{sub 2}-POA was ineffective for samples with thick thermal oxide layers, interface nitridation using N{sub 2}-POA was achieved under certain conditions, i.e., thin SiO{sub 2} layers (< 15 nm) and high annealing temperatures (>1350°C). Electrical characterizations of SiC-MOS capacitors treated with high-temperature N{sub 2}-POA revealed the same evidence of slow trap passivation and fast trap generation that occurred in NO-treated devices fabricated with the optimized nitridation conditions.
- OSTI ID:
- 22492351
- Journal Information:
- AIP Advances, Journal Name: AIP Advances Journal Issue: 9 Vol. 5; ISSN AAIDBI; ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
The Effects of Nitrogen on the Interface State Density Near the Conduction Band Edge in 4H and 6H-SiC
Passivation of Oxide Layers on 4H-SiC Using Sequential Anneals in Nitric Oxide and Hydrogen
Insights into ultraviolet-induced electrical degradation of thermally grown SiO{sub 2}/4H-SiC(0001) interface
Conference
·
Mon Jun 12 00:00:00 EDT 2000
·
OSTI ID:771405
Passivation of Oxide Layers on 4H-SiC Using Sequential Anneals in Nitric Oxide and Hydrogen
Conference
·
Wed Dec 31 23:00:00 EST 2003
·
OSTI ID:978128
Insights into ultraviolet-induced electrical degradation of thermally grown SiO{sub 2}/4H-SiC(0001) interface
Journal Article
·
Sun Jan 05 23:00:00 EST 2014
· Applied Physics Letters
·
OSTI ID:22257143