Structural and magnetic studies of nanocrystalline Y{sub 2}Ir{sub 2}O{sub 7}
Journal Article
·
· AIP Conference Proceedings
- Department of Physics, Indian Institute of Technology Kanpur, Kanpur-208016 (India)
In this paper, we discuss synthesis of Y{sub 2}Ir{sub 2}O{sub 7} nanoparticles via chemical solution process. Structural analysis shows single cubic phase with Fd-3m space group symmetry. The particle size and distribution were studied by Transmission Electron Microscopy experiments. The average particle size turns out to be 50nm, which is in good agreement with the XRD results. Magnetic characterization shows no evidence of long range ordering even in presence of strong correlations.
- OSTI ID:
- 22490323
- Journal Information:
- AIP Conference Proceedings, Vol. 1665, Issue 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cellulose-precursor synthesis of nanocrystalline Co{sub 0.5}Cu{sub 0.5}Fe{sub 2}O{sub 4} spinel ferrites
Magnetic properties of nanocrystalline Mn{sub 1-x}Zn{sub x}Fe{sub 2}O{sub 4}
Mössbauer Studies and Magnetic Properties of Cubic CuFe{sub 2}O{sub 4} Nanoparticles
Journal Article
·
Wed Feb 15 00:00:00 EST 2012
· Materials Research Bulletin
·
OSTI ID:22490323
Magnetic properties of nanocrystalline Mn{sub 1-x}Zn{sub x}Fe{sub 2}O{sub 4}
Journal Article
·
Wed Jun 24 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:22490323
+1 more
Mössbauer Studies and Magnetic Properties of Cubic CuFe{sub 2}O{sub 4} Nanoparticles
Journal Article
·
Fri Mar 15 00:00:00 EDT 2019
· Journal of Superconductivity and Novel Magnetism
·
OSTI ID:22490323
+7 more