Photoluminescence and cathodoluminescence properties of Eu{sup 3+} ions activated AMoO{sub 4} (A = Mg, Ca, Sr, Ba) phosphors
Highlights: • Under 393 nm excitation, strong red emission located at 615 nm was observed in all the samples. • The Eu{sup 3+}-activated CaMoO{sub 4} phosphor exhibited the strongest PL properties. • The CIE chromaticity coordinate of Eu{sup 3+}-activated CaMoO{sub 4} phosphor was (0.647,0.352). • The color purity of Eu{sup 3+}-activated CaMoO{sub 4} phosphor was 92.8%. • Strong CL properties were observed in the Eu{sup 3+}-activated CaMoO{sub 4} phosphor. - Abstract: Eu{sup 3+}-activated AMoO{sub 4} (A = Mg, Ca, Sr, Ba) phosphors were synthesized by a solid-state reaction method. Photoluminescence and cathodoluminescence (CL) spectra as well as X-ray diffraction patterns were measured to characterize the fabricated samples. Under 393 nm excitation, strong red emissions located at ∼615 nm corresponding to the {sup 5}D{sub 0} → {sup 7}F{sub 2} transition of Eu{sup 3+} ions were observed in all the samples. Compared with other Eu{sup 3+} ions activated AMoO{sub 4} (A = Mg, Sr, Ba) phosphors, Eu{sup 3+}-activated CaMoO{sub 4} phosphor exhibited the strongest red emission intensity with better Commission Internationale de L’Eclairage chromaticity coordinate and higher color purity. Furthermore, the CL results indicated that the Eu{sup 3+}-activated CaMoO{sub 4} phosphor had excellent luminescence properties.
- OSTI ID:
- 22475941
- Journal Information:
- Materials Research Bulletin, Vol. 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
A novel red phosphor Ca{sub 12}Al{sub 14}O{sub 32}Cl{sub 2}:Eu{sup 3+} for near UV white light-emitting diodes
Near-UV and blue wavelength excitable Mg{sub 0.6}Ca{sub 2.16}Mo{sub 0.2}W{sub 0.8}O{sub 6}: Eu{sub 0.12}{sup 3+}/Na{sub 0.12}{sup +} high efficiency red phosphors
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM COMPOUNDS
CALCIUM COMPOUNDS
CATHODOLUMINESCENCE
COLOR
COMPARATIVE EVALUATIONS
EUROPIUM ADDITIONS
EXCITATION
IMPURITIES
MAGNESIUM COMPOUNDS
MOLYBDATES
PHOSPHORS
PHOTOLUMINESCENCE
SOLIDS
SPECTRA
STRONTIUM COMPOUNDS
X-RAY DIFFRACTION