A novel red phosphor Ca{sub 12}Al{sub 14}O{sub 32}Cl{sub 2}:Eu{sup 3+} for near UV white light-emitting diodes
Graphical abstract: - Highlights: • Novel red phosphor Ca{sub 12}Al{sub 14}O{sub 32}Cl{sub 2}:Eu{sup 3+} was prepared by solid-state reaction. • Excitation spectra suggested an obvious absorption in near-ultraviolet region. • Under 392 nm excitation, the phosphors exhibited a red emission at 614 nm. • Ca{sub 12}Al{sub 14}O{sub 32}Cl{sub 2}:Eu{sup 3+} could be potentially applied in near UV white LEDs. - Abstract: A novel red phosphor Ca{sub 12}Al{sub 14}O{sub 32}Cl{sub 2}:Eu{sup 3+} was synthesized using a solid-state reaction method, and its luminescence characteristics and charge compensators effect (Li{sup +}, Na{sup +}, K{sup +}) were investigated. The excitation spectra showed a obvious absorption in near-ultraviolet region. Under 392 nm excitation, the phosphors exhibited an intense red emission at 614 nm. The Commission Internationale de l’Eclairage (CIE) chromaticity coordinates and quantum efficiency (QE) were (0.65, 0.35) and 62.3%, respectively. The good color saturation, high quantum efficiency and small thermal-quenching properties indicate that Ca{sub 12}Al{sub 14}O{sub 32}Cl{sub 2}:Eu{sup 3+} could be potentially applied in near UV white light-emitting diodes.
- OSTI ID:
- 22285134
- Journal Information:
- Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 10 Vol. 48; ISSN MRBUAC; ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Broadband sensitized white light emission of g-C{sub 3}N{sub 4}/Y{sub 2}MoO{sub 6}:Eu{sup 3+} composite phosphor under near ultraviolet excitation
Near-UV and blue wavelength excitable Mg{sub 0.6}Ca{sub 2.16}Mo{sub 0.2}W{sub 0.8}O{sub 6}: Eu{sub 0.12}{sup 3+}/Na{sub 0.12}{sup +} high efficiency red phosphors