High energy storage density performance of Ba, Sr-modified lead lanthanum zirconate titanate stannate antiferroelectric ceramics

Journal Article · Tue Oct 15 04:00:00 EDT 2013 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2013.05.083· OSTI ID:22475708

Wang, Jinfei; Yang, Tongqing; Chen, Shengchen; Li, Gang

Graphical abstract: Polarization hysteresis (P–E) loops of the (Pb{sub 0.85}Ba{sub 0.08}Sr{sub 0.03}La{sub 0.03}) (Zr{sub 0.74}Sn{sub 0.22}Ti{sub 0.04}) samples: (a) measured at different applied electric-field and (b) measured at different temperatures is shown. It is typical antiferroelectrics whose remnant polarization is zero. As the remnant polarization of AFE is small and the ceramics are accompanied by the formation of the anti-parallel domain structure, energy stored in PLZST can be effectively released. Thus we calculated the energy density from the P–E loop and obtained the power density was up to 1.2 J/cm{sup 3} at 55 °C, and at 45 °C the energy density was ∼1.24 J/cm{sup 3}. As usual, for bulk ceramics, the switching between the AFE and FE states occurs at lower field. This value is much higher than that reported previously for the PLZT bulk ceramic (0.4 J/cm{sup 3}). - Highlights: • Ba{sup 2+}, Sr{sup 2+} co-doping caused the T{sub c} of PLZST moved to the lower temperature (T{sub c} ≈ 40 °C). • The ΔE was so smaller, E{sub AF} ≈ 90 kV/cm and E{sub FA} ≈ 85 kV/cm. • Ba, Sr co-doped PLZST ceramic exhibited slanted P–E loops with a large breakdown field (100 kV/cm). • A high energy density was up to 1.2 J/cm{sup 3}. - Abstract: (Pb{sub 0.85}Ba{sub 0.08}Sr{sub 0.03}La{sub 0.03})(Zr{sub 0.74}Sn{sub 0.22}Ti{sub 0.04}) (Ba, Sr co-doped PLZST) co-doping antiferroelectric (AFE) ceramics with orthorhombic perovskite structure were prepared by the traditional solid state reaction process. It was observed that the doping of barium and strontium caused the Curie temperature of PLZST move to the lower temperature (T{sub c} ≈ 40 °C). Ba, Sr co-doped PLZST AFE ceramics exhibited excellent electrical properties, the AFE to ferroelectric (FE) transition occurred at field E{sub AF} ≈ 90 kV/cm, and the transition from FE to AFE occurred at E{sub FA} ≈ 85 kV/cm. The maximum relative permittivity was about 4800, occurring at a field near the AFE to FE transition point, with a dielectric loss of 0.006. The samples exhibited small ΔE and slanted hysteresis loops with a large breakdown field of 100 kV/cm due to Ba, Sr co-doping ceramics, and a high energy density of 1.2 J/cm{sup 3}.

• OSTI ID: 22475708
• Journal Information: Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 10 Vol. 48; ISSN MRBUAC; ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
BARIUM ADDITIONS
BREAKDOWN
CERAMICS
CURIE POINT
DENSITY
DOMAIN STRUCTURE
DOPED MATERIALS
ELECTRIC FIELDS
ENERGY DENSITY
ENERGY STORAGE
FERROELECTRIC MATERIALS
HYSTERESIS
ORTHORHOMBIC LATTICES
PERFORMANCE
PERMITTIVITY
PEROVSKITE
PLZT
POLARIZATION
STRONTIUM ADDITIONS
X-RAY DIFFRACTION