Deposition of highly textured AlN thin films by reactive high power impulse magnetron sputtering
- Department of Solid State Electronics, Ångström Laboratory, Uppsala University, Box 534, SE-752 21 Uppsala, Sweden and School of Electrical and Computer Engineering, University of Campinas, CEP 13.083-852 Campinas-SP (Brazil)
- Department of Solid State Electronics, Ångström Laboratory, Uppsala University, Box 534, SE-752 21 Uppsala (Sweden)
Aluminum nitride thin films were deposited by reactive high power impulse magnetron sputtering (HiPIMS) and pulsed direct-current on Si (100) and textured Mo substrates, where the same deposition conditions were used for both techniques. The films were characterized by x-ray diffraction and atomic force microscopy. The results show a pronounced improvement in the AlN crystalline texture for all films deposited by HiPIMS on Si. Already at room temperature, the HiPIMS films exhibited a strong preferred (002) orientation and at 400 °C, no contributions from other orientations were detected. Despite the low film thickness of only 200 nm, an ω-scan full width at half maximum value of 5.1° was achieved on Si. The results are attributed to the high ionization of sputtered material achieved in HiPIMS. On textured Mo, there was no significant difference between the deposition techniques.
- OSTI ID:
- 22392162
- Journal Information:
- Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Journal Name: Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films Journal Issue: 2 Vol. 33; ISSN 0734-2101; ISSN JVTAD6
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of deposition parameters on the structure of AlN coatings grown by reactive magnetron sputtering
A review comparing cathodic arcs and high power impulse magnetron sputtering (HiPIMS)