Synthesis and characterization of 10 nm thick piezoelectric AlN films with high c-axis orientation for miniaturized nanoelectromechanical devices
- Electrical and Computer Engineering Department, Carnegie Mellon University, Pittsburgh, Pennsylvania 15213 (United States)
The scaling of piezoelectric nanoelectromechanical systems (NEMS) is challenged by the synthesis of ultrathin and high quality piezoelectric films on very thin electrodes. We report the synthesis and characterization of the thinnest piezoelectric aluminum nitride (AlN) films (10 nm) ever deposited on ultrathin platinum layers (2–5 nm) using reactive sputtering. X-ray diffraction, high-resolution transmission electron microscopy, and fast Fourier transform analyses confirmed the proper crystal orientation, fine columnar texture, and the continuous lattice structure within individual grains in the deposited AlN nanometer thick films. The average extracted d{sub 31} piezoelectric coefficient for the synthesized films is −1.73 pC/N, which is comparable to the reported values for micron thick and highly c-axis oriented AlN films. The 10 nm AlN films were employed to demonstrate two different types of optimized piezoelectric nanoactuators. The unimorph actuators exhibit vertical displacements as large as 1.1 μm at 0.7 V for 25 μm long and 30 nm thick beams. These results have a great potential to realize miniaturized NEMS relays with extremely low voltage, high frequency resonators, and ultrasensitive sensors.
- OSTI ID:
- 22303869
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 25 Vol. 104; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Piezoelectric/ultrananocrystalline diamond heterostructures for high-performance multifunctional micro/nanoelectromechanical systems.
Piezoelectric/ultrananocrystalline diamond heterostructures for a new generation of multifunctional micro/nanoelectromechanical systems.