Controllable synthesis, growth mechanism and optical properties of the ZnSe quantum dots and nanoparticles with different crystalline phases

Journal Article · Fri Mar 15 04:00:00 EDT 2013 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2012.11.100· OSTI ID:22290378

Feng, Bo ^[1]; Yang, Jinghai ^[2]; Cao, Jian; Yang, Lili; Gao, Ming; Wei, Maobin; Liu, Yang ^[2]; Song, Hang ^[1]

---

1. Key Laboratory of Excited State Physics, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 3888 Eastern Nan-Hu Road, Changchun 130033 (China)
2. Institute of Condensed State Physics, Jilin Normal University, Siping 136000 (China)

Graphical abstract: The ZnSe quantum dots (3.5 nm) with the wurtzite structure exhibited a strong near band-edge emission (NBE) peak centered at 422 nm. The zinc blende ZnSe nanoparticles (21 nm) exhibited near-band-edge luminescence peak centered at 472 nm. Highlights: ► The results of TEM showed that the ZnSe quantum dots were about 3.5 nm. ► The ZnSe quantum dots exhibited a near band-edge emission peak centered at 422 nm. ► The ZnSe nanoparticles exhibited near-band-edge luminescence peak centered at 472 nm. - Abstract: ZnSe precursors were prepared by a solvothermal method at 180 °C without any surface-active agents. ZnSe quantum dots and nanoparticles were obtained by annealing the precursors at 300 °C for 2 h in argon atmosphere. The ZnSe quantum dots were about 3.5 nm, while the ZnSe nanoparticles were about 21 nm, as observed using TEM. The growth mechanisms for the two samples were discussed; this proved that the high coordination ability of ethylenediamine to zinc played an important role in the final phase of the products. The ZnSe quantum dots with the wurtzite structure exhibited a strong near band-edge emission (NBE) peak centered at 422 nm, which was blue-shifted in comparison to that of the bulk ZnSe, which was mainly caused by the quantum confinement effect. However, the zinc blende ZnSe nanoparticles exhibited a near-band-edge luminescence peak centered at 472 nm.

• OSTI ID: 22290378
• Journal Information: Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 3 Vol. 48; ISSN MRBUAC; ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
LUMINESCENCE
OPTICAL PROPERTIES
PARTICLES
QUANTUM DOTS
SYNTHESIS
TRANSMISSION ELECTRON MICROSCOPY
ZINC SELENIDES
ZINC SULFIDES