The influence of semiconductive binary Sb{sub 2}S{sub 3}–Yb{sub 3}S{sub 4} system on electrical conductivity property of epoxy composites
- Department of Chemical Engineering, Faculty of Engineering, Selcuk University, 42031 Konya (Turkey)
The purpose of this study is to develop the semiconductive composites. Semiconducting glass (SG) binary system Sb{sub 2}S{sub 3}–Yb{sub 3}S{sub 4} in mole ratio 1:1 was synthesized and was doped with I{sub 2}. Next, electrically conductive DGEBA-type epoxy resin (ER)/SG-filled composites and epoxy toluene oligomer (ETO) modified epoxy resin-SG filled composites were developed with 3–10 wt. % of fillers and characterized. As a result, the effects of the modifier and amount of semiconductive filler on the electrical properties of commercial epoxy resin were examined. Percolation concentration was 7 wt. % for all composites. For the SG-reinforced composites, the dispersion of the fillers is investigated by X-ray diffraction (XRD) and by scanning electron microscopy (SEM)
- OSTI ID:
- 22280357
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1599; ISSN APCPCS; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Toughened epoxy polymers: Fatigue crack propagation mechanisms. Ph.D. Thesis
Morphological and electrical properties of epoxy-based composites reinforced with exfoliated graphite