Research on pulse electrodeposition of Fe-Ni alloy
- College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China)
- School of Materials Science and Engineering, Southeast University, Nanjing 211100 (China)
Fe-Ni alloys were fabricated on steel substrates by means of pulse electrodeposition in sulfate solutions. The layers were electrodeposited using different peak current densities, duty cycles and frequencies. Fe contents, microhardnesses and crystalline phases were examined systematically. The Fe content in the deposit decreased and the microhardness increased with increasing duty cycle and peak current density. The pulse frequency had little effect on Fe content but led to a slight decrease in microhardness. X-ray diffraction patterns show that the crystalline phases vary with changes in peak current density and duty cycle but are barely influenced by frequency. When the peak current density or duty cycle is relatively low, crystalline Fe-Ni alloy and pure Fe phases coexist; the pure Fe phases disappear as the peak current density or duty cycle increases. At still larger peak current densities or duty cycles, crystalline Fe-Ni alloy and pure Ni phases coexist.
- OSTI ID:
- 22251121
- Journal Information:
- AIP Advances, Vol. 4, Issue 3; Other Information: (c) 2014 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Pulsed electrodeposition of Ni-Mo alloys
Pulsed electrodeposition. Final report