Photoelectric and luminescence properties of GaSb-Based nanoheterostructures with a deep Al(As)Sb/InAsSb/Al(As)Sb quantum well grown by metalorganic vapor-phase epitaxy
- Russian Academy of Sciences, Ioffe Physical-Technical Institute (Russian Federation)
- Academy of Sciences of the Czech Republic, Institute of Physics (Czech Republic)
The luminescence and photoelectric properties of heterostructures with a deep Al(As)Sb/InAsSb/Al(As)Sb quantum well grown on n-GaSb substrates by metalorganic vapor-phase epitaxy are investigated. Intense superlinear luminescence and increased optical power as a function of the pump current in the photon energy range of 0.6-0.8 eV are observed at temperatures of T = 77 and 300 K. The photoelectric, current-voltage, and capacitance characteristics of these heterostructures are studied in detail. The photosensitivity is examined with photodetectors operating in the photovoltaic mode in the spectral range of 0.9-2.0 {mu}m. The sensitivity maximum at room temperature is observed at a wavelength of 1.55 {mu}m. The quantum efficiency, detectivity, and response time of the photodetectors were estimated. The quantum efficiency and detectivity at the peak of the photosensitivity spectrum are as high as {eta} = 0.6-0.7 and D{sub {lambda}max}{sup *} = (5-7) Multiplication-Sign 10{sup 10} cm Hz{sup 1/2} W{sup -1}, respectively. The photodiode response time determined as the rise time of the photoresponse pulse from 0.1 to the level 0.9 is 100-200 ps. The photodiode transmission bandwidth is 2-3 GHz. Photodetectors with a deep Al(As)Sb/InAsSb/Al(As)Sb quantum well grown on n-GaSb substrates are promising foruse in heterodyne detection systems and in information technologies.
- OSTI ID:
- 22210583
- Journal Information:
- Semiconductors, Journal Name: Semiconductors Journal Issue: 8 Vol. 47; ISSN SMICES; ISSN 1063-7826
- Country of Publication:
- United States
- Language:
- English
Similar Records
Photovoltaic detector based on type II heterostructure with deep AlSb/InAsSb/AlSb quantum well in the active region for the midinfrared spectral range
Electroluminescence in p-InAs/AlSb/InAsSb/AlSb/p(n)-GaSb type II heterostructures with deep quantum wells at the interface
High performance photodiodes based on InAs/InAsSb type-II superlattices for very long wavelength infrared detection
Journal Article
·
Mon Feb 14 23:00:00 EST 2011
· Semiconductors
·
OSTI ID:22004864
Electroluminescence in p-InAs/AlSb/InAsSb/AlSb/p(n)-GaSb type II heterostructures with deep quantum wells at the interface
Journal Article
·
Thu Jan 14 23:00:00 EST 2010
· Semiconductors
·
OSTI ID:21562367
High performance photodiodes based on InAs/InAsSb type-II superlattices for very long wavelength infrared detection
Journal Article
·
Mon Jun 23 00:00:00 EDT 2014
· Applied Physics Letters
·
OSTI ID:22303835