Enhanced photocatalytic efficiency in zirconia buffered n-NiO/p-NiO single crystalline heterostructures by nanosecond laser treatment
- Department of Materials Science and Engineering, NC State University, EB-1, Raleigh, North Carolina 27695-7907 (United States)
We report the formation of NiO based single crystalline p-n junctions with enhanced photocatalytic activity induced by pulsed laser irradiation. The NiO epilayers were grown on Si(001) substrates buffered with cubic yttria-stabilized zirconia (c-YSZ) by using pulsed laser deposition. The NiO/c-YSZ/Si heterostructures were subsequently laser treated by 5 pulses of KrF excimer laser (pulse duration = 25 Multiplication-Sign 10{sup -9} s) at lower energies. Microstructural studies, conducted by X-ray diffraction ({theta}-2{theta} and {phi} techniques) and high resolution transmission electron microscope, showed a cube-on-cube epitaxial relationship at the c-YSZ/Si interface; the epitaxial relationship across the NiO/c-YSZ interface was established as NiO<111 > Double-Vertical-Line Double-Vertical-Line c-YSZ<001> and in-plane NiO<110> Double-Vertical-Line Double-Vertical-Line c-YSZ<100>. Electron microscopy studies showed that the interface between the laser annealed and the pristine region as well as the NiO/c-YSZ interface was atomically sharp and crystallographically continuous. The formation of point defects, namely oxygen vacancies and NiO, due to the coupling of the laser photons with the NiO epilayers was confirmed by XPS. The p-type electrical characteristics of the pristine NiO epilayers turned to an n-type behavior and the electrical conductivity was increased by one order of magnitude after laser treatment. Photocatalytic activity of the pristine (p-NiO/c-YSZ/Si) and the laser-annealed (n-NiO/p-NiO/c-YSZ/Si) heterostructures were assessed by measuring the decomposition rate of 4-chlorophenol under UV light. The photocatalytic reaction rate constants were determined to be 0.0059 and 0.0092 min{sup -1} for the as-deposited and the laser-treated samples, respectively. The enhanced photocatalytic efficiency was attributed to the suppressed charge carrier recombination in the NiO based p-n junctions and higher electrical conductivity. Besides, the oxygen vacancies ease the adsorption of 4-chlorophenol, hydroxyl, and water molecules to the surface. Thus, n-NiO/p-NiO single crystalline catalysts can be introduced as a potent candidate to remediate the environmental pollution.
- OSTI ID:
- 22163054
- Journal Information:
- Journal of Applied Physics, Vol. 113, Issue 23; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ferroelectric and ferromagnetic properties in BaTiO{sub 3} thin films on Si (100)
Interface-structure of the Si/SiC heterojunction grown on 6H-SiC
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ADSORPTION
CATALYSTS
ELECTRIC CONDUCTIVITY
ENERGY BEAM DEPOSITION
EPITAXY
LASER RADIATION
LAYERS
MONOCRYSTALS
NICKEL OXIDES
PHOTOCATALYSIS
PHOTOCHEMISTRY
P-N JUNCTIONS
RECOMBINATION
SEMICONDUCTOR MATERIALS
SUBSTRATES
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
X-RAY PHOTOELECTRON SPECTROSCOPY
YTTRIUM OXIDES
ZIRCONIUM OXIDES