Asymmetric interfacial abruptness in N-polar and Ga-polar GaN/AlN/GaN heterostructures
- Materials Department, University of California, Santa Barbara, California 93106 (United States)
- Department of Electrical and Computer Engineering, University of California, Santa Barbara, California 93106 (United States)
In this letter, we report on the interfacial abruptness of GaN/AlN/GaN heterostructures with pulsed laser atom probe tomography (APT). The samples were grown by plasma-assisted molecular beam epitaxy (MBE) under both metal-rich and N-rich conditions on both Ga-polar (0001) GaN templates and N-polar (0001) GaN substrates. An NH{sub 3} assisted MBE technique was involved to grow similar Ga-polar and N-polar structures on GaN:Fe substrates and GaN/Al{sub 2}O{sub 3} templates, respectively, for a comparison study. We find in all cases the interface with net positive polarization charge was chemically abrupt, whereas the interface with net negative polarization charge was diffuse. We discuss the implications on device design and performance. These data validate the efficiency of APT in studying interfaces for better performance in devices.
- OSTI ID:
- 22089402
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 9 Vol. 101; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Molecular beam homoepitaxy of N-polar AlN: Enabling role of aluminum-assisted surface cleaning