Effect of residual stress on the ferroelectric property of (Pb{sub 0.90}La{sub 0.10})Ti{sub 0.975}O{sub 3} thin films
- Department of Materials Science, Sichuan University, Chengdu 610064 (China)
Highly (001)-, (100)-, (101)-, and (110)-oriented (Pb{sub 0.90}La{sub 0.10})Ti{sub 0.975}O{sub 3} (PLT) thin films were deposited on the LaNiO{sub 3}(001)/Pt(111)/Ti/SiO{sub 2}/Si(100), LaNiO{sub 3}/SiO{sub 2}/Si(100), PbTiO{sub 3}/Pt(111)/Ti/SiO{sub 2}/Si(100), and LaNiO{sub 3}(110)/Pt(111)/Ti/SiO{sub 2}/Si(100) substrates by rf magnetron sputtering. The orientation dependence of ferroelectric properties of the PLT films was investigated. The result shows that the (001)-oriented PLT thin films exhibit enhanced ferroelectric properties (2P{sub r}=61.1 {mu}C/cm{sup 2} and 2E{sub c}=179 kV/cm). The residual stress of the PLT thin films with different orientations was measured by x-ray diffraction (sin{sup 2} {psi} method) for illuminating the related physical mechanisms. The result shows that the enhanced ferroelectric properties of (001)-oriented PLT thin films should be attributed to low residual stress.
- OSTI ID:
- 21190067
- Journal Information:
- Journal of Applied Physics, Journal Name: Journal of Applied Physics Journal Issue: 5 Vol. 105; ISSN JAPIAU; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of orientation on the dielectric and piezoelectric properties of 0.2Pb(Mg{sub 1/3}Nb{sub 2/3})O{sub 3}--0.8Pb(Zr{sub 0.5}Ti{sub 0.5})O{sub 3} thin films
Properties and orientation of antiferroelectric lead zirconate thin films grown by MOCVD.