Microstructure and magnetic properties of FePt-SiO{sub 2} granular films with Ag addition
Journal Article
·
· Journal of Applied Physics
- Graduate School of Pure and Applied Sciences, University of Tsukuba, Tsukuba 305-8577 (Japan)
Perpendicularly anisotropic L1{sub 0}-ordered FePt-SiO{sub 2} granular films with an average grain size of 15 nm and a relatively narrow size distribution were prepared by cosputtering Fe, Pt, and SiO{sub 2} on MgO (001) substrates at 700 deg. C. By reducing the substrate temperature to 500 deg. C, the average grain size was further refined to 6.2 nm with a standard deviation of 1.7 nm; however, the FePt particles remained as an A1 disordered phase. Alloying Ag to the FePt particles and increasing the Ar gas pressure in the sputtering chamber were found to be both beneficial for enhancing the L1{sub 0} ordering while keeping the fine granular structure.
- OSTI ID:
- 21064519
- Journal Information:
- Journal of Applied Physics, Vol. 103, Issue 2; Other Information: DOI: 10.1063/1.2828032; (c) 2008 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of CrRu-SiO{sub x} underlayer with MgO intermediate layer on the microstructure and magnetic properties of FePt-C thin film
FePt-C nanogranular films for perpendicular magnetic recording
Microstructure and Magnetic Properties of FePt-MgO Multilayer Thin Films
Journal Article
·
Fri Apr 01 00:00:00 EDT 2011
· Journal of Applied Physics
·
OSTI ID:21064519
+2 more
FePt-C nanogranular films for perpendicular magnetic recording
Journal Article
·
Wed Apr 01 00:00:00 EDT 2009
· Journal of Applied Physics
·
OSTI ID:21064519
Microstructure and Magnetic Properties of FePt-MgO Multilayer Thin Films
Journal Article
·
Sat Jan 01 00:00:00 EST 2005
· Microscopy and Microanalysis
·
OSTI ID:21064519
+2 more