Study on properties of CaO-SiO{sub 2}-B{sub 2}O{sub 3} system glass-ceramic
Journal Article
·
· Materials Research Bulletin
OSTI ID:21000656
- College of Material Science and Engineering, Nanjing University of Technology, Nanjing 210009, Jiangsu (China)
Low temperature co-fired ceramic (LTCC) is prepared by sintering a glass selected from CaO-SiO{sub 2}-B{sub 2}O{sub 3} system, and its sintered bodies are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). It is found that the optimal sintering temperature for this glass-ceramic is 820 deg. C for 15 min, and the major phases of this material are CaSiO{sub 3}, CaB{sub 2}O{sub 4} and SiO{sub 2}. The glass-ceramic possesses excellent dielectric properties: {epsilon} {sub r} = 6.5, tan {delta} < 2 x 10{sup -3} at 10 MHz, temperature coefficient of dielectric constant about -51 x 10{sup -6} deg. C{sup -1} and coefficient of thermal expansion about 8 x 10{sup -6} deg. C{sup -1} at 20-400 deg. C. Thus, this material is supposed to be suitable for the tape casting process and be compatible with Ag electrode, which could be used as the LTCC materials for the application in wireless communications.
- OSTI ID:
- 21000656
- Journal Information:
- Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 6 Vol. 42; ISSN MRBUAC; ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Study on properties of Ba{sub x}Sm{sub y}Ti{sub 7}O{sub 20} ceramics with CaO-SiO{sub 2}-B{sub 2}O{sub 3} glass
Crystallization, densification and dielectric properties of CaO–MgO–Al{sub 2}O{sub 3}–SiO{sub 2} glass with ZrO{sub 2} as nucleating agent
Effect of B{sub 2}O{sub 3}-Bi{sub 2}O{sub 3}-SiO{sub 2}-ZnO glass on the sintering and microwave dielectric properties of 0.83ZnAl{sub 2}O{sub 4}-0.17TiO{sub 2}
Journal Article
·
Wed Mar 04 23:00:00 EST 2009
· Materials Research Bulletin
·
OSTI ID:21199711
Crystallization, densification and dielectric properties of CaO–MgO–Al{sub 2}O{sub 3}–SiO{sub 2} glass with ZrO{sub 2} as nucleating agent
Journal Article
·
Sun Dec 14 23:00:00 EST 2014
· Materials Research Bulletin
·
OSTI ID:22420714
Effect of B{sub 2}O{sub 3}-Bi{sub 2}O{sub 3}-SiO{sub 2}-ZnO glass on the sintering and microwave dielectric properties of 0.83ZnAl{sub 2}O{sub 4}-0.17TiO{sub 2}
Journal Article
·
Tue Apr 01 00:00:00 EDT 2008
· Materials Research Bulletin
·
OSTI ID:21068236