Transparent conducting Al-doped ZnO thin films prepared by magnetron sputtering with dc and rf powers applied in combination
- Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)
A newly developed Al-doped ZnO (AZO) thin-film magnetron-sputtering deposition technique that decreases resistivity, improves resistivity distribution, and produces high-rate depositions has been demonstrated by dc magnetron-sputtering depositions that incorporate rf power (dc+rf-MS), either with or without the introduction of H{sub 2} gas into the deposition chamber. The dc+rf-MS preparations were carried out in a pure Ar or an Ar+H{sub 2} (0%-2%) gas atmosphere at a pressure of 0.4 Pa by adding a rf component (13.56 MHz) to a constant dc power of 80 W. The deposition rate in a dc+rf-MS deposition incorporating a rf power of 150 W was approximately 62 nm/min, an increase from the approximately 35 nm/min observed in dc magnetron sputtering with a dc power of 80 W. A resistivity as low as 3x10{sup -4} {omega} cm and an improved resistivity distribution could be obtained in AZO thin films deposited on substrates at a low temperature of 150 deg. C by dc+rf-MS with the introduction of hydrogen gas with a content of 1.5%. This article describes the effects of adding a rf power component (i.e., dc+rf-MS deposition) as well as introducing H{sub 2} gas into dc magnetron-sputtering preparations of transparent conducting AZO thin films.
- OSTI ID:
- 20979473
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Vol. 25, Issue 4; Other Information: DOI: 10.1116/1.2748809; (c) 2007 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of nitrogen ion implantation time on tungsten films deposited by DC magnetron sputtering on AISI 410 martensitic stainless steel
ZnO Thin Film Ga s Sensor for CO