Cross-sectional transmission electron microscopy method and studies of implant damage in single crystal diamond
- Materials Science and Engineering Department, University of Florida, Gainesville, Florida 32611-6400 (United States)
Few transmission electron microscopy (TEM) studies of single crystal diamond have been reported, most likely due to the time and difficulty involved in sample preparation. A method is described for creating a TEM cross section of single crystal diamond using a focused ion beam and in situ lift-out. The method results in samples approximately 10 {mu}m long by 3 {mu}m deep with an average thickness of 100-300 nm. The total time to prepare a cross-sectional TEM sample of diamond is less than 5 h. The method also allows for additional thinning to facilitate high resolution TEM imaging, and can be applied to oddly shaped diamond samples. This sample preparation technique has been applied to the study of ion implantation damage in single crystal diamond and its evolution upon annealing. High-pressure-high-temperature diamonds were implanted with Si{sup +} at an energy of 1 MeV and a temperature of 30 deg. C. One sample, with a (110) surface, was implanted with a dose of 1x10{sup 14} Si cm{sup -2} and annealed at 950 deg. C for 10 and 40 min. No significant defect formation or evolution was discernible by cross-sectional transmission electron microscopy. Another sample, with a (100) orientation, was implanted with 1 MeV at 1x10{sup 15} Si cm{sup -2} and annealed at 1050 deg. C for 10 min. Prior to annealing, a heavily damaged but still crystalline region was observed. Upon annealing, the sample showed no signs of conversion either to an amorphous form of carbon or to graphite. This is unexpected as the energy and dose are above the previously reported graphitization threshold for diamond. Higher annealing temperatures and possibly a high vacuum will be required for future study of defect formation, evolution, and phase transformations in ion-implanted single crystal diamond.
- OSTI ID:
- 20777318
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Vol. 24, Issue 4; Other Information: DOI: 10.1116/1.2209659; (c) 2006 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
Behavior of implanted strontium in yttria-stabilized zirconia
Impact of the end of range damage from low energy Ge preamorphizing implants on the thermal stability of shallow boron profiles