Fabrication of highly selective tungsten oxide ammonia sensors
Tungsten oxide is shown to be a very promising material for the fabrication of highly selective ammonia sensors. Films of WO{sub 3} were deposited onto a silicon substrate by means of the drop-coating method. Then, the films were annealed in dry air at two different temperatures (300 and 400 C). X-ray photoelectron spectroscopy was used to investigate the composition of the films. Tungsten appeared both in WO{sub 2} and WO{sub 3} oxidation states, but the second state was clearly dominant. Scanning electron microscopy results showed that the oxide was amorphous or nanocrystalline. The WO{sub 3}-based devices were sensitive to ammonia vapors when operated between 250 and 350 C. The optimal operating temperature for the highest sensitivity to ammonia was 300 C. Furthermore, when the devices were operated at 300 C, their sensitivity to other reducing species such as ethanol, methane, toluene, and water vapor was significantly lower, and this resulted in a high selectivity to ammonia. A model for the sensing mechanisms of the fabricated sensors is proposed.
- Research Organization:
- Univ. Rovira i Virgili, Tarragona (ES)
- OSTI ID:
- 20023354
- Journal Information:
- Journal of the Electrochemical Society, Vol. 147, Issue 2; Other Information: PBD: Feb 2000; ISSN 0013-4651
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tungsten oxide (WO{sub 3}) thin films for application in advanced energy systems
Preparation of amorphous electrochromic tungsten oxide and molybdenum oxide by plasma enhanced chemical vapor deposition