Susceptibility of conventional pressure vessel steel to hydrogen-induced cracking and stress-oriented hydrogen-induced cracking in hydrogen sulfide-containing diglycolamine solutions
Hydrogen-induced cracking (HIC) and stress-oriented hydrogen-induced cracking (SOHIC) tests were conducted on a conventional type A516-70 (UNS K02700) pressure vessel steel exposed to hydrogen sulfide (H{sub 2}S)-containing diglycolamine (DGA) gas-sweetening environments. Base-line HIC and SOHIC tests were conducted in NACE TM0284-96 Solution A. For the SOHIC tests, four-point double-beam specimens were stressed to 60%, 80%, or 100% of the yield strength of the steel to study the effect of applied stress. Test conditions included solutions containing 70 wt% DGA and 500 ppm H{sub 2}S to {ge} 0.45 M-H{sub 2}S/M-DGA and temperatures of 25 C, 45 C, and 80 C. Corrosion rates of the steel were calculated from weight loss of the HIC specimens to compare the severity of the test environment with the actual service environment. Cracks were characterized in terms of crack length ratio (CLR), crack thickness ratio (CTR), and crack sensitivity ratio (CSR). Results indicated that conventional type A516-70 pressure vessel steel was not susceptible to HIC or SOHIC in various H{sub 2}-containing DGA solutions at the temperatures studied.
- Research Organization:
- Ohio State Univ., Columbus, OH (US)
- OSTI ID:
- 20002041
- Journal Information:
- Corrosion (Houston), Journal Name: Corrosion (Houston) Journal Issue: 11 Vol. 55; ISSN CORRAK
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation of the susceptibility of conventional ASTM A515-70 pressure vessel steel to HIC and SOHIC in H{sub 2}S - containing DGA solutions
Test procedures for evaluation of resistance of steels to cracking in wet H{sub 2}S environments
Avoid H[sub 2]S corrosion in refinery vessels
Conference
·
Thu Jul 01 00:00:00 EDT 1999
·
OSTI ID:20002648
Test procedures for evaluation of resistance of steels to cracking in wet H{sub 2}S environments
Book
·
Fri Dec 30 23:00:00 EST 1994
·
OSTI ID:83055
Avoid H[sub 2]S corrosion in refinery vessels
Journal Article
·
Tue Dec 31 23:00:00 EST 1991
· Hydrocarbon Processing; (United States)
·
OSTI ID:6814961