Transport properties of discontinuous Co{sub 80}Fe{sub 20}/Al{sub 2}O{sub 3} multilayers, prepared by ion beam sputtering
Journal Article
·
· IEEE Transactions on Magnetics (Institute of Electrical and Electronics Engineers)
Ion beam sputtered Co{sub 80}Fe{sub 20}(t)/Al{sub 2}O{sub 3}(30 {angstrom}) multilayers were obtained. The Co{sub 80}Fe{sub 20} layers become discontinuous for nominal thicknesses T {le} 18{angstrom}. Tunnel magnetoresistance was measured in CIP and CPP geometries, reaching up to 6.5% at room temperature and 11% at 15 K, for as-deposited films in CIP geometry. The temperature dependence of MR was found quite different for the two geometries: fairly strong in the CIP case and almost absent in the CPP geometry. A model is proposed to explain these large differences in behavior.
- Research Organization:
- Univ. do Porto (PT)
- OSTI ID:
- 20000664
- Journal Information:
- IEEE Transactions on Magnetics (Institute of Electrical and Electronics Engineers), Vol. 35, Issue 5Pt1; Conference: 1999 international magnetics conference (Intermag '99), Kyongju (KR), 05/18/1999--05/21/1999; Other Information: PBD: Sep 1999; ISSN 0018-9464
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetic structure determination for annealed Ni{sub 80}Fe{sub 20}/Ag multilayers using polarized-neutron reflectivity
Stress in sputtered Co{sub 90}Fe{sub 10}/Ag GMR multilayers
High yield Cu-Co CPP GMR multilayer sensors
Conference
·
Sun Dec 31 00:00:00 EST 1995
·
OSTI ID:20000664
+5 more
Stress in sputtered Co{sub 90}Fe{sub 10}/Ag GMR multilayers
Book
·
Thu May 01 00:00:00 EDT 1997
·
OSTI ID:20000664
+1 more
High yield Cu-Co CPP GMR multilayer sensors
Technical Report
·
Wed Jan 15 00:00:00 EST 1997
·
OSTI ID:20000664
+3 more