Flux versus Hydrothermal Growth: Polymorphism of A 2 (UO 2 )Si 2 O 6 (A = Rb, Cs)
Journal Article
·
· Inorganic Chemistry
- Department of Chemistry and Biochemistry, University of South Carolina, Columbia, South Carolina 29208, United States
Not provided.
- Research Organization:
- Univ. of South Carolina, Columbia, SC (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- SC0008664
- OSTI ID:
- 1534531
- Journal Information:
- Inorganic Chemistry, Vol. 56, Issue 3; ISSN 0020-1669
- Publisher:
- American Chemical Society (ACS)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Observation of the Same New Sheet Topology in Both the Layered Uranyl Oxide-Phosphate Cs11[(UO2)12(PO4)3O13] and the Layered Uranyl Oxyfluoride-Phosphate Rb11[(UO2)12(PO4)3O12F2] Prepared by Flux Crystal Growth
Crystal Growth of Alkali Uranyl Borates from Molten Salt Fluxes: Characterization and Ion Exchange Behavior of A 2 (UO 2 )B 2 O 5 (A = Cs, Rb, K)
From {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}O(MoO{sub 4}){sub 4}]{sup 6-} to {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]{sup 6-} infinite chains in A{sub 6}U{sub 2}Mo{sub 4}O{sub 21} (A=Na, K, Rb, Cs) compounds: Synthesis and crystal structure of Cs{sub 6}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]
Journal Article
·
Wed Aug 21 00:00:00 EDT 2019
· Frontiers in Chemistry
·
OSTI ID:1534531
+1 more
Crystal Growth of Alkali Uranyl Borates from Molten Salt Fluxes: Characterization and Ion Exchange Behavior of A 2 (UO 2 )B 2 O 5 (A = Cs, Rb, K)
Journal Article
·
Fri Apr 10 00:00:00 EDT 2020
· Inorganic Chemistry
·
OSTI ID:1534531
+5 more
From {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}O(MoO{sub 4}){sub 4}]{sup 6-} to {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]{sup 6-} infinite chains in A{sub 6}U{sub 2}Mo{sub 4}O{sub 21} (A=Na, K, Rb, Cs) compounds: Synthesis and crystal structure of Cs{sub 6}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]
Journal Article
·
Sun May 15 00:00:00 EDT 2011
· Journal of Solid State Chemistry
·
OSTI ID:1534531
+1 more