Crystal Growth of Alkali Uranyl Borates from Molten Salt Fluxes: Characterization and Ion Exchange Behavior of A 2 (UO 2 )B 2 O 5 (A = Cs, Rb, K)
Journal Article
·
· Inorganic Chemistry
- Center for Hierarchical Waste form Materials, Columbia, South Carolina 29208, United States; Department of Chemistry and Biochemistry, University of South Carolina, Columbia, South Carolina 29208, United States
- Center for Hierarchical Waste form Materials, Columbia, South Carolina 29208, United States; Kazuo Inamori School of Engineering, Alfred University, Alfred, New York 14802, United States
- Department of Chemistry and Biochemistry, University of South Carolina, Columbia, South Carolina 29208, United States
- Center for Hierarchical Waste form Materials, Columbia, South Carolina 29208, United States; Department of Mechanical Engineering, University of South Carolina, Columbia, South Carolina 29208, United States
Not provided.
- Research Organization:
- Energy Frontier Research Centers (EFRC) (United States). Center for Hierarchical Waste Form Materials (CHWM); Univ. of South Carolina, Columbia, SC (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- SC0016574
- OSTI ID:
- 1767600
- Journal Information:
- Inorganic Chemistry, Vol. 59, Issue 9; ISSN 0020-1669
- Publisher:
- American Chemical Society (ACS)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Observation of the Same New Sheet Topology in Both the Layered Uranyl Oxide-Phosphate Cs11[(UO2)12(PO4)3O13] and the Layered Uranyl Oxyfluoride-Phosphate Rb11[(UO2)12(PO4)3O12F2] Prepared by Flux Crystal Growth
Molten salt flux synthesis and crystal structure of a new open-framework uranyl phosphate Cs{sub 3}(UO{sub 2}){sub 2}(PO{sub 4})O{sub 2}: Spectroscopic characterization and cationic mobility studies
From {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}O(MoO{sub 4}){sub 4}]{sup 6-} to {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]{sup 6-} infinite chains in A{sub 6}U{sub 2}Mo{sub 4}O{sub 21} (A=Na, K, Rb, Cs) compounds: Synthesis and crystal structure of Cs{sub 6}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]
Journal Article
·
Wed Aug 21 00:00:00 EDT 2019
· Frontiers in Chemistry
·
OSTI ID:1767600
+1 more
Molten salt flux synthesis and crystal structure of a new open-framework uranyl phosphate Cs{sub 3}(UO{sub 2}){sub 2}(PO{sub 4})O{sub 2}: Spectroscopic characterization and cationic mobility studies
Journal Article
·
Mon Apr 15 00:00:00 EDT 2013
· Journal of Solid State Chemistry
·
OSTI ID:1767600
From {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}O(MoO{sub 4}){sub 4}]{sup 6-} to {sub {infinity}}{sup 1}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]{sup 6-} infinite chains in A{sub 6}U{sub 2}Mo{sub 4}O{sub 21} (A=Na, K, Rb, Cs) compounds: Synthesis and crystal structure of Cs{sub 6}[(UO{sub 2}){sub 2}(MoO{sub 4}){sub 3}(MoO{sub 5})]
Journal Article
·
Sun May 15 00:00:00 EDT 2011
· Journal of Solid State Chemistry
·
OSTI ID:1767600
+1 more