Synthesis and Characterization of Pure and Doped Ceria Films by Sol-gel and Sputtering
Synthesis and Characterization of Pure and Doped Ceria Films by Sol-gel and Sputtering. KURT T. KOCH (University of Missouri, Rolla, MO, 65409) LAXMIKANT SARAF (Environmental and Molecular Science Laboratory (Part of Pacific Northwest National Laboratory), Richland, Washington 99352). Pure and doped Ceria are known for their ability to gain or lose Oxygen, which is of interest to the Solid Oxide Fuel Cell (SOFC) and catalyst community. Current efforts are focused in SOFCs to reduce the operating temperature of the cell while maintaining ionic conduction. Ceria is known for its high ionic conductivity in the intermediate temperature region. (600-800 C) We have prepared pure and doped Ceria films by Sol-gel and magnetron sputtering methods. These films were characterized by X-ray diffraction (XRD), nuclear reaction analysis (NRA), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and Oxygen conduction measurements. We have observed greater volume diffusion in nanocrystalline Ceria compared to bulk polycrystalline films as a result of low density. Near surface diffusion properties with increasing temperature indicate a decrease in the volume diffusion as a result of grain growth. However, a linear increase in O2 content at {approx}600nm depth was observed and can be correlated to the redistribution of O2 in the samples. Surface roughness of <111> and <200> oriented Ceria films on Al2O3 and YSZ was observed to be 0.13nm and 0.397nm, respectively. In the case of Ceria grown on YSZ, structural properties from XRD results showed a highly oriented structure with cube on cube growth. XRD results from Ceria grown on Al2O3 showed an oriented state near the surface. structure whose degree of orientation appeared to be partially dependent on substrate temperature. Preliminary XPS results indicate reduction in Ceria from the Ce4+ to Ce3+ state near the surface.
- Research Organization:
- Pacific Northwest National Lab., Richland, WA (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 15015209
- Report Number(s):
- PNNL-SA-39174; KP1301030; TRN: US200509%%346
- Journal Information:
- Journal of Undergraduate Research, Vol. 4; Other Information: PBD: 1 Dec 2004
- Country of Publication:
- United States
- Language:
- English
Similar Records
Growth and characterization of highly oriented gadolinia-doped ceria (111) thin films on zirconia (111)/sapphire (0001) substrates
Nanostructured ceria based thin films ({<=}1 {mu}m) As cathode/electrolyte interfaces