Evaluation of rhenium joining methods
Coupons of rhenium-to-Cl03 flat plate joints, formed by explosive and diffusion bonding, were evaluated in a series of shear tests. Shear testing was conducted on as-received, thermally-cycled (100 cycles, from 21 to 1100 C), and thermally-aged (3 and 6 hrs at 1100 C) joint coupons. Shear tests were also conducted on joint coupons with rhenium and/or Cl03 electron beam welded tabs to simulate the joint`s incorporation into a structure. Ultimate shear strength was used as a figure of merit to assess the effects of the thermal treatment and the electron beam welding of tabs on the joint coupons. All of the coupons survived thermal testing intact and without any visible degradation. Two different lots of as-received, explosively-bonded joint coupons had ultimate shear strengths of 281 and 310 MPa and 162 and 223 MPa, respectively. As-received, diffusion-bonded coupons had ultimate shear strengths of 199 and 348 MPa. For the most part, the thermally-treated and rhenium weld tab coupons had shear strengths slightly reduced or within the range of the as-received values. Coupons with Cl03 weld tabs experienced a significant reduction in shear strength. The degradation of strength appeared to be the result of a poor heat sink provided during the electron beam welding. The Cl03 base material could not dissipate heat as effectively as rhenium, leading to the formation of a brittle rhenium-niobium intermetallic.
- Research Organization:
- NASA Lewis Research Center, Cleveland, OH (United States)
- OSTI ID:
- 147154
- Report Number(s):
- N-96-12351; NASA-TM-107055; NAS-1.15:107055; AIAA-Paper-95-2397; E-9903; CONF-950720-; CNN: RTOP 232-02-03; TRN: 9612351
- Resource Relation:
- Conference: AIAA/SAE/ASME joint propulsion conference and exhibit, San Diego, CA (United States), 10-12 Jul 1995; Other Information: PBD: Sep 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Joining techniques for a reduced activation 12Cr steel for inertial fusion energy
Fusion joining of thermoplastic composite wind turbine blades: Lap-shear bond characterization