Hierarchically Porous Carbon Materials for CO 2 Capture: The Role of Pore Structure
- Pacific Northwest National Laboratory, 902 Battelle Boulevard, Richland, Washington 99352, United States
With advances in porous carbon synthesis techniques, hierarchically porous carbon (HPC) materials are being utilized as relatively new porous carbon sorbents for CO2 capture applications. These HPC materials were used as a platform to prepare samples with differing textural properties and morphologies to elucidate structure-property relationships. It was found that high microporous content, rather than overall surface area was of primary importance for predicting good CO2 capture performance. Two HPC materials were analyzed, each with near identical high surface area (~2700 m2/g) and colossally high pore volume (~10 cm3/g), but with different microporous content and pore size distributions, which led to dramatically different CO2 capture performance. Overall, large pore volumes obtained from distinct mesopores were found to significantly impact adsorption performance. From these results, an optimized HPC material was synthesized that achieved a high CO2 capacity of ~3.7 mmol/g at 25°C and 1 bar.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1422275
- Report Number(s):
- PNNL-SA-129228
- Journal Information:
- Industrial and Engineering Chemistry Research, Vol. 57, Issue 4; ISSN 0888-5885
- Publisher:
- American Chemical Society (ACS)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure–Property Correlation of Hierarchically Porous Carbons for Fluorocarbon Adsorption
Pore size effects on the sorption of supercritical carbon dioxide in mesoporous CPG-10 silica