Superficial Velocity Effects on HZ-PAN and AgZ-PAN for Kr/Xe Capture
Nearly all previous testing of HZ-PAN and AgZ-PAN was conducted at the same flow rate in order to maintain consistency among tests. This testing was sufficient for sorbent capacity determinations, but did not ensure that sorbents were capable of functioning under a range of flow regimes. Tests were conducted on both HZ-PAN and AgZ-PAN at superficial velocities between 20 and 700 cm/min. For HZ-PAN, Kr capacity increased from 60 mmol/kg to 110 mmol/kg as superficial velocity increased from 21 to 679 cm/min. Results for AgZ-PAN were similar, with capacity ranging from 72 to 124 mmol/kg over the same range of superficial. These results are promising for scaling up to process flows, demonstrating flexibility to operate in a broad range of superficial velocities while maintaining sorbent capacity. While preparing for superficial velocity testing it was also discovered that AgZ-PAN Xe capacity, previously observed to diminish over time, could be recovered with increased desorption temperature. Further, a substantial Xe capacity increase was observed. Previous room temperature capacities in the range of 22-25 mmol Xe/kg AgZ-PAN were increased to over 60 mmol Xe/kg AgZ-PAN. While this finding has not yet been fully explored to optimize activation and desorption temperatures, it is encouraging.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- AC07-05ID14517
- OSTI ID:
- 1261015
- Report Number(s):
- INL/EXT-16-38331; TRN: US1601568
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preliminary Desorption studies for HZ-PAN and AgZ-PAN
Cycle Testing of AgZ-PAN and HZ-PAN