Record current density of 344 A mm −2 at 4.2 K and 17 T in CORC ® accelerator magnet cables
Journal Article
·
· Superconductor Science and Technology
- Sponsoring Organization:
- USDOE Office of Science (SC), High Energy Physics (HEP)
- Grant/Contract Number:
- SC0007891; SC0009545; SC0014009
- OSTI ID:
- 1245286
- Journal Information:
- Superconductor Science and Technology, Journal Name: Superconductor Science and Technology Vol. 29 Journal Issue: 5; ISSN 0953-2048
- Publisher:
- IOP PublishingCopyright Statement
- Country of Publication:
- United Kingdom
- Language:
- English
Cited by: 49 works
Citation information provided by
Web of Science
Web of Science
Similar Records
Engineering current density in excess of 200 A mm
−2
at 20 T in CORC
®
magnet cables containing RE-Ba
2
Cu
3
O
7−
δ
tapes with 38
μ
m thick substrates
Development of ReBCO-CORC Wires With Current Densities of 400–600 A/mm $^2$ at 10 T and 4.2 K
Introduction of the next generation of CORC ® wires with engineering current density exceeding 650 A mm -2 at 12 T based on SuperPower’s ReBCO tapes containing substrates of 25 μ m thickness
Journal Article
·
Fri Oct 23 00:00:00 EDT 2015
· Superconductor Science and Technology
·
OSTI ID:1245286
+5 more
Development of ReBCO-CORC Wires With Current Densities of 400–600 A/mm $^2$ at 10 T and 4.2 K
Journal Article
·
Sun Apr 01 00:00:00 EDT 2018
· IEEE Transactions on Applied Superconductivity
·
OSTI ID:1245286
+2 more
Introduction of the next generation of CORC ® wires with engineering current density exceeding 650 A mm -2 at 12 T based on SuperPower’s ReBCO tapes containing substrates of 25 μ m thickness
Journal Article
·
Mon Feb 17 00:00:00 EST 2020
· Superconductor Science and Technology
·
OSTI ID:1245286
+7 more