Engineering current density in excess of 200 A mm −2 at 20 T in CORC ® magnet cables containing RE-Ba 2 Cu 3 O 7− δ tapes with 38 μ m thick substrates
Journal Article
·
· Superconductor Science and Technology
- Sponsoring Organization:
- USDOE Office of Science (SC), High Energy Physics (HEP)
- Grant/Contract Number:
- SC0007891; SC0009545
- OSTI ID:
- 1241442
- Journal Information:
- Superconductor Science and Technology, Journal Name: Superconductor Science and Technology Vol. 28 Journal Issue: 12; ISSN 0953-2048
- Publisher:
- IOP PublishingCopyright Statement
- Country of Publication:
- United Kingdom
- Language:
- English
Cited by: 24 works
Citation information provided by
Web of Science
Web of Science
Similar Records
Introduction of the next generation of CORC ® wires with engineering current density exceeding 650 A mm -2 at 12 T based on SuperPower’s ReBCO tapes containing substrates of 25 μ m thickness
Record current density of 344 A mm −2 at 4.2 K and 17 T in CORC ® accelerator magnet cables
Superconducting transition width (Δ T c ) characteristics of 25 mol% Zr-added (Gd, Y)Ba 2 Cu 3 O 7− δ superconductor tapes with high in-field critical current density at 30 K
Journal Article
·
Mon Feb 17 00:00:00 EST 2020
· Superconductor Science and Technology
·
OSTI ID:1241442
+7 more
Record current density of 344 A mm −2 at 4.2 K and 17 T in CORC ® accelerator magnet cables
Journal Article
·
Mon Apr 04 00:00:00 EDT 2016
· Superconductor Science and Technology
·
OSTI ID:1241442
+4 more
Superconducting transition width (Δ T c ) characteristics of 25 mol% Zr-added (Gd, Y)Ba 2 Cu 3 O 7− δ superconductor tapes with high in-field critical current density at 30 K
Journal Article
·
Fri Nov 18 00:00:00 EST 2016
· Superconductor Science and Technology
·
OSTI ID:1241442
+6 more