Relative contributions of several cathodic reactions to the anodic dissolution of electrogalvanized steel
Conference
·
OSTI ID:124432
- Inland Steel Flat Products Co., East Chicago, IN (United States)
- Illinois Inst. of Technology, Chicago, IL (United States). IIT Center
Zero-resistance ammeter measurements and a 2{sup 3} full factorial statistical experimental design were used to determine the effects of pH, oxygen, and red rust on the cathodic half cell reaction on corroding electrogalvanized steel. Analysis of variance indicated that the red rust reduction reaction was dominant. The recently developed galvanic corrosion/mechanical wedging model for underfilm corrosion of painted galvanized steel is thus supported.
- OSTI ID:
- 124432
- Report Number(s):
- CONF-950304--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Relative contributions of several cathodic reactions to the anodic dissolution of electrogalvanized steel
Measurement of underfilm corrosion propagation by use of spotface paint damage
Behavior of painted steel and aluminum sheet in laboratory corrosion tests
Journal Article
·
Thu Feb 29 23:00:00 EST 1996
· Corrosion
·
OSTI ID:215643
Measurement of underfilm corrosion propagation by use of spotface paint damage
Book
·
Tue Oct 31 23:00:00 EST 1995
·
OSTI ID:124428
Behavior of painted steel and aluminum sheet in laboratory corrosion tests
Book
·
Tue Oct 31 23:00:00 EST 1995
·
OSTI ID:124418