Strong correlation between J c ( T , H || c ) and J c (77 K, 3 T|| c ) in Zr-added (Gd, Y)BaCuO coated conductors at temperatures from 77 down to 20 K and fields up to 9 T
Journal Article
·
· Superconductor Science and Technology
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- Grant/Contract Number:
- AR0000196; AR0000337
- OSTI ID:
- 1238874
- Journal Information:
- Superconductor Science and Technology, Vol. 28, Issue 8; ISSN 0953-2048
- Publisher:
- IOP PublishingCopyright Statement
- Country of Publication:
- United Kingdom
- Language:
- English
Cited by: 22 works
Citation information provided by
Web of Science
Web of Science
Similar Records
Superconducting transition width (Δ
T
c
) characteristics of 25 mol% Zr-added (Gd, Y)Ba
2
Cu
3
O
7−
δ
superconductor tapes with high in-field critical current density at 30 K
Strongly enhanced vortex pinning from 4 to 77 K in magnetic fields up to 31 T in 15 mol.% Zr-added (Gd, Y)-Ba-Cu-O superconducting tapes
Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K
Journal Article
·
Fri Nov 18 00:00:00 EST 2016
· Superconductor Science and Technology
·
OSTI ID:1238874
+6 more
Strongly enhanced vortex pinning from 4 to 77 K in magnetic fields up to 31 T in 15 mol.% Zr-added (Gd, Y)-Ba-Cu-O superconducting tapes
Journal Article
·
Tue Apr 01 00:00:00 EDT 2014
· APL Materials
·
OSTI ID:1238874
+6 more
Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K
Journal Article
·
Tue Mar 11 00:00:00 EDT 2014
· Superconductor Science and Technology
·
OSTI ID:1238874
+5 more