Joining of alumina ceramics and nickel alloy
Conference
·
OSTI ID:115550
Joining of alumina ceramics to nickel alloy was made using the various types of Ag-Cu-Ti brazing filler metal. Ti-containing brazing filler metal was produced by physical vapor deposition (PVD) method on the joining area of the alumina ceramics. The joinability of the brazing filler metal was estimated by its mechanical properties. And the composition and structure of the ceramic-metal bond zone in the alumina ceramics-nickel alloy joints were analyzed by SEM, EPMA and X-ray diffraction examinations. Some of brazing filler metal achieved the highest shear strength 100 MPa at room temperature. The elemental distributions of the interface between alumina ceramics and Ag-Cu-Ti brazing filler metal was shown to form the reaction layer consisting titanium oxide.
- OSTI ID:
- 115550
- Report Number(s):
- CONF-9404233--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Braze material for joining ceramic to metal and ceramic to ceramic surfaces and joined ceramic to metal and ceramic to ceramic article
Braze material for joining ceramic to metal and ceramic to ceramic surfaces and joined ceramic to metal and ceramic to ceramic article
Joining of ceramics for advanced heavy-duty diesels
Patent
·
Mon Dec 31 23:00:00 EST 1990
·
OSTI ID:867804
Braze material for joining ceramic to metal and ceramic to ceramic surfaces and joined ceramic to metal and ceramic to ceramic article
Patent
·
Tue May 07 00:00:00 EDT 1991
·
OSTI ID:7277621
Joining of ceramics for advanced heavy-duty diesels
Technical Report
·
Fri Feb 28 23:00:00 EST 1986
·
OSTI ID:5601962