Automated Data Collection for Determining Statistical Distributions of Module Power Undergoing Potential-Induced Degradation: Preprint
Conference
·
OSTI ID:1150195
We propose a method for increasing the frequency of data collection and reducing the time and cost of accelerated lifetime testing of photovoltaic modules undergoing potential-induced degradation (PID). This consists of in-situ measurements of dark current-voltage curves of the modules at elevated stress temperature, their use to determine the maximum power at 25 degrees C standard test conditions (STC), and distribution statistics for determining degradation rates as a function of stress level. The semi-continuous data obtained by this method clearly show degradation curves of the maximum power, including an incubation phase, rates and extent of degradation, precise time to failure, and partial recovery. Stress tests were performed on crystalline silicon modules at 85% relative humidity and 60 degrees C, 72 degrees C, and 85 degrees C. Activation energy for the mean time to failure (1% relative) of 0.85 eV was determined and a mean time to failure of 8,000 h at 25 degrees C and 85% relative humidity is predicted. No clear trend in maximum degradation as a function of stress temperature was observed.
- Research Organization:
- National Renewable Energy Laboratory (NREL), Golden, CO.
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy Solar Energy Technologies Office
- DOE Contract Number:
- AC36-08GO28308;
- OSTI ID:
- 1150195
- Report Number(s):
- NREL/CP-5J00-62468
- Conference Information:
- Presented at the 24th Workshop on Crystalline Silicon Solar Cells & Modules: Materials and Processes, 27-30 July 2014, Breckenridge, Colorado
- Country of Publication:
- United States
- Language:
- English
Similar Records
Testing and Analysis for Lifetime Prediction of Crystalline Silicon PV Modules Undergoing Degradation by System Voltage Stress: Preprint
Potential induced degradation in c-Si glass-glass modules after extended damp heat stress
Potential-Induced Degradation-Delamination Mode in Crystalline Silicon Modules: Preprint
Conference
·
Sat Jun 30 20:00:00 EDT 2012
·
OSTI ID:1051918
Potential induced degradation in c-Si glass-glass modules after extended damp heat stress
Journal Article
·
Tue Mar 14 20:00:00 EDT 2023
· Solar Energy
·
OSTI ID:2007050
Potential-Induced Degradation-Delamination Mode in Crystalline Silicon Modules: Preprint
Conference
·
Tue Mar 20 20:00:00 EDT 2018
·
OSTI ID:1429979