Energy Saving Melting and Revert Reduction Technology (Energy-SMARRT): Clean Steel Casting Production

Technical Report · Tue Dec 31 04:00:00 EST 2013

DOI:https://doi.org/10.2172/1126492· OSTI ID:1126492

Kuyucak, Selcuk ^[1]; Li, Delin ^[2]

---

1. Natural Resources Canada, Hamilton, ON (Canada). CanmetMATERIALS; Advanced Technology Institute
2. Natural Resources Canada, Hamilton, ON (Canada). CanmetMATERIALS

Inclusions in steel castings can cause rework, scrap, poor machining, and reduced casting performance, which can obviously result in excess energy consumption. Significant progress in understanding inclusion source, formation and control has been made. Inclusions can be defined as non-metallic materials such as refractory, sand, slag, or coatings, embedded in a metallic matrix. This research project has focused on the mold filling aspects to examine the effects of pouring methods and gating designs on the steel casting cleanliness through water modeling, computer modeling, and melting/casting experiments. Early in the research project, comprehensive studies of bottom-pouring water modeling and low-alloy steel casting experiments were completed. The extent of air entrainment in bottom-poured large castings was demonstrated by water modeling. Current gating systems are designed to prevent air aspiration. However, air entrainment is equally harmful and no prevention measures are in current practice. In this study, new basin designs included a basin dam, submerged nozzle, and nozzle extension. The entrained air and inclusions from the gating system were significantly reduced using the new basin method. Near the end of the project, there has been close collaboration with Wescast Industries Inc., a company manufacturing automotive exhaust components. Both computer modeling using Magma software and melting/casting experiments on thin wall turbo-housing stainless steel castings were completed in this short period of time. Six gating designs were created, including the current gating on the pattern, non-pressurized, partially pressurized, naturally pressurized, naturally pressurized without filter, and radial choke gating without filter, for Magma modeling. The melt filling velocity and temperature were determined from the modeling. Based on the simulation results, three gating designs were chosen for further melting and casting experiments on the same casting pattern using the lip pouring method. It was observed again that gating designs greatly influenced the melt filling velocity and the number of inclusion defects. The radial choked gating showed improvements in casting cleanliness and yield over the other gatings, even though no mold filters were used in the gating system.

• Research Organization: Natural Resources Canada, Hamilton, ON (Canada). CanmetMATERIALS
• Sponsoring Organization: USDOE Office of Energy Efficiency and Renewable Energy (EERE), Energy Efficiency Office. Advanced Materials & Manufacturing Technologies Office (AMMTO)
• Contributing Organization: Harrison Steel Castings Co, Attica, IN; Wescast Industries Inc., Brantford, Ontario, Canada
• DOE Contract Number: FC36-04GO14230
• OSTI ID: 1126492
• Country of Publication: United States
• Language: English

Related Subjects

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATION
Casting
Metal Casting
Steel Casting