Soft-Templating Synthesis and Properties of Mesoporous Alumina-Titania

Journal Article · Thu Dec 31 23:00:00 EST 2009 · Microporous and Mesoporous Materials

DOI:https://doi.org/10.1016/j.micromeso.2009.08.018· OSTI ID:1081624

Morris, Stacy M ^[1]; Horton, Jr, Joe A ^[2]; Jaroniec, Mietek ^[1]

---

1. Kent State University
2. ORNL

Mesoporous alumina-titania materials, having various molar compositions of aluminum and titanium, were synthesized via cooperative self-assembly of the corresponding metal alkoxides and Pluronic P123 triblock copolymer (soft template) in ethanolic solution under acidic conditions. The resulting mixed metal oxides possess ordered mesopores at low to equal molar compositions of titanium in relation to aluminum (up to 50%) and worm-like mesostructures at higher molar compositions of titanium (50-75%). In addition, these mesoporous oxides exhibit high BET surface areas (up to 438 m2/g), large pore widths (from 7.37 to 18.55 nm) and pore volumes (from 0.16 to 0.64 cm3/g), narrow pore size distributions, crystalline pore walls and high thermal stability.

• Research Organization: Oak Ridge National Laboratory (ORNL); Center for Nanophase Materials Sciences
• Sponsoring Organization: SC USDOE - Office of Science (SC)
• DOE Contract Number: AC05-00OR22725
• OSTI ID: 1081624
• Journal Information: Microporous and Mesoporous Materials, Journal Name: Microporous and Mesoporous Materials Journal Issue: 1-3 Vol. 128; ISSN 1387-1811
• Publisher: Elsevier
• Country of Publication: United States
• Language: English

Related Subjects

Alumina
Alumina-titania
Aluminum titanium oxide
Mesoporous
Mixed metal oxide
Mixed oxide
Ordered mesoporous oxide
Soft-templating
Tielite
Titania