Challenges in Fabrication of Mesoporous Carbon Films with Ordered Cylindrical Pores via Phenolic Oligomer Self-Assembly with Triblock Copolymers
- On Semi
Mesoporous phenol formaldehyde (PF) polymer resin and carbon films are prepared by a solution self-assembly of PF oligomers with amphiphilic triblock copolymers. After thermopolymerization of the PF to cross-link the network, the films show an ordered morphology as determined by X-ray diffraction and grazing incidence small-angle X-ray scattering (GISAXS). Our results show that the amphiphilic triblock copolymer template greatly influences the stability of the final porous mesostructures. The pyrolysis of the two-dimensional (2-D) hexagonal films with p6mm symmetry templated by Pluronic F127 yields a disordered porous structure following the template removal. Conversely, films templated by Pluronic P123 can exhibit well-ordered cylindrical pores after the template removal, but the solution composition range to yield ordered cylindrical mesopores is significantly reduced (nearly 70%) for thin films in comparison to bulk powders. We propose two dominant difficulties in fabricating well-ordered cylindrical mesopores in films: first, the stress from contraction during the pyrolysis can lead to a collapse of the mesostructure if the wall thickness is insufficient, and second, the surface wetting behavior in thin films leads to a small compositional range.
- Research Organization:
- Advanced Photon Source (APS), Argonne National Laboratory (ANL), Argonne, IL (US)
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 1002445
- Journal Information:
- ACS Nano, Journal Name: ACS Nano Journal Issue: (1) ; 01, 2010 Vol. 4
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Stabilizing Surfactant Templated Cylindrical Mesopores in Polymer and Carbon Films through Composite Formation with Silica Reinforcement
Soft-Templating Synthesis and Properties of Mesoporous Alumina-Titania