Source fabrication and lifetime for Li+ ion beams extracted from alumino-silicate sources
A space-charge-limited beam with current densities (J) exceeding 1 mA/cm2 have been measured from lithium alumino-silicate ion sources at a temperature of ~1275 °C. At higher extraction voltages, the source appears to become emission limited with J ≥ 1.5 mA/cm2, and J increases weakly with the applied voltage. A 6.35 mm diameter source with an alumino-silicate coating, ≤0.25 mm thick, has a measured lifetime of ~40 h at ~1275 °C, when pulsed at 0.05 Hz and with pulse length of ~6 μs each. At this rate, the source lifetime was independent of the actual beam charge extracted due to the loss of neutral atoms at high temperature. Finally, the source lifetime increases with the amount of alumino-silicate coated on the emitting surface, and may also be further extended if the temperature is reduced between pulses.
- Research Organization:
- Ernest Orlando Lawrence Berkeley National Laboratory, Berkeley, CA (US)
- Sponsoring Organization:
- Accelerator& Fusion Research Division
- DOE Contract Number:
- AC02-05CH11231
- OSTI ID:
- 1076798
- Report Number(s):
- LBNL-5373E
- Journal Information:
- Review of Scientific Instruments, Journal Name: Review of Scientific Instruments Journal Issue: 4 Vol. 83; ISSN 0034-6748; ISSN RSINAK
- Publisher:
- American Institute of Physics (AIP)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Source fabrication and lifetime for Li{sup +} ion beams extracted from alumino-silicate sources
A HIGH CURRENT DENSITY LI+ ALUMINO-SILICATE ION SOURCE FOR TARGET HEATING EXPERIMENTS