A HIGH CURRENT DENSITY LI+ ALUMINO-SILICATE ION SOURCE FOR TARGET HEATING EXPERIMENTS
The NDCX-II accelerator for target heating experiments has been designed to use a large diameter ({approx_equal} 10.9 cm) Li{sup +} doped alumino-silicate source with a pulse duration of 0.5 {micro}s, and beam current of {approx_equal} 93 mA. Characterization of a prototype lithium alumino-silicate sources is presented. Using 6.35mm diameter prototype emitters (coated on a {approx_equal} 75% porous tungsten substrate), at a temperature of {approx_equal} 1275 C, a space-charge limited Li{sup +} beam current density of {approx_equal} 1 mA/cm{sup 2} was measured. At higher extraction voltage, the source is emission limited at around {approx_equal} 1.5 mA/cm{sup 2}, weakly dependent on the applied voltage. The lifetime of the ion source is {approx_equal} 50 hours while pulsing the extraction voltage at 2 to 3 times per minute. Measurements show that the life time of the ion source does not depend only on beam current extraction, and lithium loss may be dominated by neutral loss or by evaporation. The life time of a source is around {ge} 10 hours in a DC mode extraction, and the extracted charge is {approx_equal} 75% of the available Li in the sample. It is inferred that pulsed heating may increase the life time of a source.
- Research Organization:
- Ernest Orlando Lawrence Berkeley National Laboratory, Berkeley, CA (US)
- Sponsoring Organization:
- Accelerator& Fusion Research Division
- DOE Contract Number:
- AC02-05CH11231
- OSTI ID:
- 1010546
- Report Number(s):
- LBNL-3996E
- Country of Publication:
- United States
- Language:
- English
Similar Records
Source fabrication and lifetime for Li+ ion beams extracted from alumino-silicate sources
Source fabrication and lifetime for Li+ ion beams extracted from alumino-silicate sources