Biaxial Flexural Strength of Poled Lead Zirconate Titanate under High Electric Field with Extended Field Range
- ORNL
In the present work, as-received poled lead zirconate titanate, or PZT 5A, was examined using ball-on-ring (BoR) mechanical testing coupled with an electric field. Electric fields in the range of 4Ec (Ec, coercive field) with controlled loading paths were applied, and mechanical tests at a substantial number of characteristic electric field levels were conducted. Commercial electronic liquid FC-40 was used to prevent the setup from dielectric breakdown under a high electric field. Weibull strength distribution was used to interpret the mechanical strength data. The data showed that the strength levels of the PZT-5A tested under OC (open circuit) in air and in FC-40 were almost the same. It was further revealed that , for the studied cases, the effect of loading history on the biaxial flexural strength of the PZT was significant in -Ec, but not in OC or zero field as well as 4Ec . An asymmetry V curve was observed for the characteristic strength-electric field graph, and the bottom of V curve was located near the negative coercive field. Microscopy analysis showed that surface-located volume-distributed flaws were the strength limiter and responsible for the failure of the tested PZT under electromechanical loadings.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1055534
- Journal Information:
- Ceramics International, Vol. 39, Issue 2; ISSN 0272-8842
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Electric Field and Biaxial Flexure on the Failure of Poled Lead Zirconate Titanate
MECHANICAL STRENGTH RESPONSES OF POLED LEAD ZIRCONATE TITANATE UNDER EXTREME ELECTRIC FIELD AND VARIOUS TEMPERATURE CONDITIONS