Strength Properties of Aged Poled Lead Zirconate Titanate Subjected to Electromechanical Loadings
- ORNL
Electric field and aging time are two important factors that affect the mechanical strength and long-term reliability of lead zirconate titanate or PZT actuators. In the present work, a commercial PZT-5A aged four years was examined using ball-on-ring (BoR) mechanical testing under coupled electric fields. The electric field range of -3E{sub c} to +3E{sub c} (E{sub c}, coercive electric field) was studied (i.e., -3E{sub c}, -E{sub c}, 0, +E{sub c}, +2E{sub c}, and +3E{sub c}) with a controlled electric loading path. A Weibull distribution was used to interpret the mechanical strength data. With an electric field preloaded from 0 to -3E{sub c}, it was found that subsequent increases in the electric field resulted in an asymmetrical V-shaped curve of mechanical strength against the electric field. The bottom of the V curve was located near the zero electric field level. Microscopy analysis showed that pores were the strength limiter for the tested PZT under electromechanical loadings.
- Research Organization:
- Oak Ridge National Laboratory (ORNL)
- Sponsoring Organization:
- EE USDOE - Office of Energy Efficiency and Renewable Energy (EE)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1050889
- Journal Information:
- Smart Materials and Structures, Journal Name: Smart Materials and Structures Journal Issue: 11 Vol. 21; ISSN 0964-1726
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Electric Field and Biaxial Flexure on the Failure of Poled Lead Zirconate Titanate
MECHANICAL STRENGTH RESPONSES OF POLED LEAD ZIRCONATE TITANATE UNDER EXTREME ELECTRIC FIELD AND VARIOUS TEMPERATURE CONDITIONS