Title: Interdiffusion and Intrinsic Diffusion in the Mg-Al System

Journal Article · · Metallurgical and Materials Transactions A

Solid-to-solid diffusion couples were assembled and annealed to examine the diffusion between pure Mg (99.96%) and Al (99.999%). Diffusion anneals were carried out at 300 , 350 , and 400 C for 720, 360, and 240 hours, respectively. Optical and scanning electron microscopes were utilized to identify the formation of the intermetallic phases, -Al12Mg17 and -Al3Mg2 and absence of the -phase in the diffusion couples. Thicknesses of the -Al12Mg17 and -Al3Mg2 phases were measured and the parabolic growth constants were calculated to determine the activation energies for the growth, 165 and 86 KJ/mole, respectively. Concentration profiles were determined with electron microprobe analysis using pure elemental standards. Composition-dependent interdiffusion coefficients in Mg-solid solution, -Al12Mg17 and - Al3Mg2 and Al-solid solutions were calculated based on the Boltzmann-Matano analysis. Average effective interdiffusion coefficients for each phase were also calculated, and the magnitude was the highest for the -Al3Mg2 phase, followed by -Al12Mg17, Al-solid solution and Mg-solid solution. Intrinsic diffusion coefficients based on Huemann s analysis (e.g., marker plane) were determined for the ~38 at.% Mg in the -Al3Mg2 phase. Activation energies and the pre-exponential factors for the inter- and intrinsic diffusion coefficients were calculated for the temperature range examined. The -Al3Mg2 phase was found to have the lowest activation energies for growth and interdiffusion among all four phases studied. At the marker location in the -Al3Mg2 phase, the intrinsic diffusion of Al was found to be faster than that of Mg. Extrapolations of the impurity diffusion coefficients in the terminal solid solutions were made and compared to the available self- and impurity diffusion data from literature. Thermodynamic factor, tracer diffusion coefficients and atomic mobilities at the marker plane composition were approximated using available literature values of Mg activity in the -Al3Mg2 phase.

Research Organization:
Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Sponsoring Organization:
USDOE Office of Energy Efficiency and Renewable Energy (EERE)
DOE Contract Number:
DE-AC05-00OR22725
OSTI ID:
1054995
Journal Information:
Metallurgical and Materials Transactions A, Vol. 43, Issue 11; ISSN 1073--5623
Country of Publication:
United States
Language:
English

Similar Records

Interdiffusion in the Ta-W system
Journal Article · Fri Nov 01 00:00:00 EST 1985 · J. Appl. Phys.; (United States) · OSTI ID:1054995

Interdiffusion and impurity diffusion in polycrystalline Mg solid solution with Al or Zn
Journal Article · Wed Jan 01 00:00:00 EST 2014 · Journal of Alloys and Compounds · OSTI ID:1054995

Interdiffusion in a bulk couple of lead and lead--50 wt % indium alloy
Journal Article · Thu Jul 01 00:00:00 EDT 1976 · Acta Metall.; (United States) · OSTI ID:1054995