Interdiffusion and impurity diffusion in polycrystalline Mg solid solution with Al or Zn

Journal Article · Tue Dec 31 23:00:00 EST 2013 · Journal of Alloys and Compounds

DOI:https://doi.org/10.1016/j.jallcom.2014.07.193· OSTI ID:1154852

Kammerer, Catherine ^[1]; Kulkarni, Nagraj S ^[2]; Warmack, Robert J Bruce ^[2]; Sohn, Yong Ho ^[3]

---

1. University of Central Florida, Orlando
2. ORNL
3. University of Central Florida

Interdiffusion and impurity diffusion in Mg binary solid solutions, Mg(Al) and Mg(Zn) were investigated at temperatures ranging from 623 to 723 K. Interdiffusion coef cients were determined via the Boltzmann Matano Method using solid-to-solid diffusion couples assembled with polycrystalline Mg and Mg(Al) or Mg(Zn) solid solutions. In addition, the Hall method was employed to extrapolate the impurity diffusion coef cients of Al and Zn in pure polycrystalline Mg. For all diffusion couples, electron micro-probe analysis was utilized for the measurement of concentration pro les. The interdiffusion coef cient in Mg(Zn) was higher than that of Mg(Al) by an order of magnitude. Additionally, the interdiffusion coef cient increased signi cantly as a function of Al content in Mg(Al) solid solution, but very little with Zn content in Mg(Zn) solid solution. The activation energy and pre-exponential factor for the average effective interdiffusion coef cient in Mg(Al) solid solution were determined to be 186.8 ( 0.9) kJ/mol and 7.69 x 10-1 ( 1.80 x 10-1) m2/s, respectively, while those determined for Mg(Zn) solid solution were 139.5 ( 4.0) kJ/mol and 1.48 x 10-3 ( 1.13 x 10-3) m2/s. In Mg, the Zn impurity diffusion coef cient was an order of magnitude higher than the Al impurity diffusion coef cient. The activation energy and pre-exponential factor for diffusion of Al impurity in Mg were determined to be 139.3 ( 14.8) kJ/mol and 6.25 x 10-5 ( 5.37 x 10-4) m2/s, respectively, while those for diffusion of Zn impurity in Mg were determined to be 118.6 ( 6.3) kJ/mol and 2.90 x 10-5 ( 4.41 x 10-5) m2/s.

• Research Organization: Oak Ridge National Laboratory (ORNL)
• Sponsoring Organization: EE USDOE - Office of Energy Efficiency and Renewable Energy (EE)
• DOE Contract Number: AC05-00OR22725
• OSTI ID: 1154852
• Journal Information: Journal of Alloys and Compounds, Journal Name: Journal of Alloys and Compounds Vol. 617; ISSN 0925-8388
• Country of Publication: United States
• Language: English