Evaluation of Alumina-Forming Austenitic Foil for Advanced Recuperators
- ORNL
- Capstone Turbines
A corrosion- and creep-resistant austenitic stainless steel has been developed for advanced recuperator applications. By optimizing the Al and Cr contents, the alloy is fully austenitic for creep strength while allowing the formation of a chemically stable external alumina scale at temperatures up to 900 C. An alumina scale eliminates long-term problems with the formation of volatile Cr oxy-hydroxides in the presence of water vapor in exhaust gas. As a first step in producing foil for primary surface recuperators, three commercially cast heats have been rolled to 100 m thick foil in the laboratory to evaluate performance in creep and oxidation testing. Results from initial creep testing are presented at 675 C and 750 C, showing excellent creep strength compared with other candidate foil materials. Laboratory exposures in humid air at 650 800 C have shown acceptable oxidation resistance. A similar oxidation behavior was observed for sheet specimens of these alloys exposed in a modified 65 kW microturbine for 2871 h. One composition that showed superior creep and oxidation resistance has been selected for the preparation of a commercial batch of foil. DOI: 10.1115/1.4002827
- Research Organization:
- Oak Ridge National Laboratory (ORNL)
- Sponsoring Organization:
- EE USDOE - Office of Energy Efficiency and Renewable Energy (EE)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1024733
- Journal Information:
- Journal of Engineering for Gas Turbines & Power, Journal Name: Journal of Engineering for Gas Turbines & Power Journal Issue: 10 Vol. 133; ISSN 0742-4795
- Country of Publication:
- United States
- Language:
- English
Similar Records
Alumina-forming Austenitic Alloys for Advanced Recuperators
High Temperature Oxidation Behavior of Fe- and Ni-Based Alloy Foils in Water Vapor at 850 °C