Hydrogen production over Ni/ceria-supported catalysts by partial oxidation of methane

Journal Article · Tue Dec 01 04:00:00 EST 2009 · INTERNATIONAL JOURNAL OF HYRDROGEN ENERGY

DOI:https://doi.org/10.1016/j.ijhydene.2009.10.019· OSTI ID:1012924

Salazar, Villalpando MD; B, Reyes

The catalytic performance of Ni dispersed on ceria-doped supports, (Ce0.88La0.12) O2-x, (Ce0.91Gd0.09) O2-x, (Ce0.71Gd0.29) O2-x, (Ce0.56Zr0.44) O2-x and pure ceria, was tested for the catalytic partial oxidation of Methane (CPOX). The catalysts were characterized by Brunauer Emmett Teller (BET), X-ray diffraction (XRD), temperature programmed reduction (TPR) and temperature programmed oxidation (TPO). Ni/ (Ce0.56Zr0.44) O2-x showed higher Hydrogen production than the Ni/Gadolinium-doped catalysts, which may be due to its higher reducibility and surface area. By enhancing the support reducibility in Ni/dopedceria catalysts, their catalytic activity is promoted because the availability of surface lattice oxygen is increased, which can participate in the formation of CO and H2. It was also found that Ni/(Ce0.56Zr0.44) O2-x showed higher catalytic performance after redox pretreatments. Similarly, a higher amount of H2 or O2 was consumed during hydrogenation and oxidation pretreatments, respectively. This may be correlated to re-dispersion of metallic particles and changes on the metal-support interface. In addition, it was observed that the ionic conductivity of Ni/(Ce0.56Zr0.44) O2-x had an effect on the amount of carbon formed during the CPOX reaction at oxygen concentrations lower than the stoichiometric required, O/C ratios lower than 0.6. Its high oxygen mobility may have accelerated the surface oxidation reactions of carbon by reactive oxygen species, thus, inhibiting carbon growth on the catalyst surface

• Research Organization: National Energy Technology Laboratory - In-house Research; National Energy Technology Laboratory (NETL), Pittsburgh, PA, and Morgantown, WV (United States)
• Sponsoring Organization: USDOE Assistant Secretary for Fossil Energy (FE)
• OSTI ID: 1012924
• Report Number(s): netltpr-2734
• Journal Information: INTERNATIONAL JOURNAL OF HYRDROGEN ENERGY, Journal Name: INTERNATIONAL JOURNAL OF HYRDROGEN ENERGY Journal Issue: 24 Vol. 34
• Country of Publication: United States
• Language: English

Related Subjects

Partial oxidation of methane Redox treatment Nickel Ceria Temperature programmed oxidation