Nanostructured energetic materials derived from sol-gel chemistry
Initiation and detonation properties are dramatically affected by an energetic material's microstructural properties. Sol-gel chemistry allows intimacy of mixing to be controlled and dramatically improved over existing methodologies. One material goal is to create very high power energetic materials which also have high energy densities. Using sol-gel chemistry we have made a nanostructured composite energetic material. Here a solid skeleton of fuel, based on resorcinol-formaldehyde, has nanocrystalline ammonium perchlorate, the oxidizer, trapped within its pores. At optimum stoichiometry it has approximately the energy density of HMX. Transmission electron microscopy indicated no ammonium perchlorate crystallites larger than 20 nm while near-edge soft x-ray absorption microscopy showed that nitrogen was uniformly distributed, at least on the scale of less than 80 nm. Small-angle neutron scattering studies were conducted on the material. Those results were consistent with historical ones for this class of nanostructured materials. The average skeletal primary particle size was on the order of 2.7 nm, while the nanocomposite showed the growth of small 1 nm size crystals of ammonium perchlorate with some clustering to form particles greater than 10 nm.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 15002503
- Report Number(s):
- UCRL-JC-136924; TRN: US0401906
- Resource Relation:
- Conference: 31st International Annual Conference of ICT, Karlsruhe (DE), 06/27/2000--06/30/2000; Other Information: PBD: 15 Mar 2000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Aerogels, emulsions, and composites: Controlling structure with organic sol-gel chemistry
Aerogels, emulsions, and composites: Controlling structure with organic sol-gel chemistry